Trans. Nonferrous Met. Soc. China 24(2014) 1653−1658 Influence of Li addition on mechanical property and aging precipitation behavior of Al−3.5Cu−1.5Mg alloy Yun-lai DENG, Jin-long YANG, Si-yu LI, Jin ZHANG, Xin-ming ZHANG School of Materials Science and Engineering, Central South University, Changsha 410083, China Received 22 May 2013; accepted 18 March 2014 Abstract: The influence of Li addition on mechanical property and aging precipitation behavior of Al−3.5Cu−1.5Mg alloy was investigated by tensile test, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and high resolution transmission electron microscopy (HRTEM). The results show that the tensile strength can be significantly improved with the slightly decreased ductility and the form of fracture morphology is converted from ductile fracture into ductile/brittle mixed fracture by adding 1.0% Li. Besides, the peak aging time at 185 °C is delayed from 12 to 24 h and the main precipitation phase S(Al2CuMg) is converted into S (Al CuMg)+δ(Al Li), while the formation of S(Al CuMg) is delayed. 2 3 2 Key words: aluminum alloy; Al−3.5Cu−1.5Mg alloy; Li; aging behavior; mechanical properties Lithium is the lightest metallic element, which 1 Introduction reduces the density and increases the modulus of Al-based alloys. The presence of Li in Al−Cu−Mg alloy Al−Cu−Mg