《Oxidation of in situ synthesized TiC particle-reinforced titanium matrix composites》.pdf
- 1、本文档共7页,可阅读全部内容。
- 2、原创力文档(book118)网站文档一经付费(服务费),不意味着购买了该文档的版权,仅供个人/单位学习、研究之用,不得用于商业用途,未经授权,严禁复制、发行、汇编、翻译或者网络传播等,侵权必究。
- 3、本站所有内容均由合作方或网友上传,本站不对文档的完整性、权威性及其观点立场正确性做任何保证或承诺!文档内容仅供研究参考,付费前请自行鉴别。如您付费,意味着您自己接受本站规则且自行承担风险,本站不退款、不进行额外附加服务;查看《如何避免下载的几个坑》。如果您已付费下载过本站文档,您可以点击 这里二次下载。
- 4、如文档侵犯商业秘密、侵犯著作权、侵犯人身权等,请点击“版权申诉”(推荐),也可以打举报电话:400-050-0827(电话支持时间:9:00-18:30)。
查看更多
《Oxidation of in situ synthesized TiC particle-reinforced titanium matrix composites》.pdf
Materials Science and Engineering A 404 (2005) 42–48
Oxidation of in situ synthesized TiC particle-reinforced
titanium matrix composites
Yexia Qin a,∗, Weijie Lu a , Di Zhang a , Jining Qin a , Bo Jib
a State Key Laboratory of Metal Matrix Composites, Shanghai JiaoTong University, Shanghai 200030, PR China
b Shanghai No. 5 Steel Co. Ltd., Bao Steel Group, Shanghai 200940, PR China
Received in revised form 11 May 2005; accepted 19 May 2005
Abstract
The oxidation behavior of TiC particle reinforced titanium matrix composites (TMCs) was studied in a temperature range 550–650 ◦C in
atmosphere. The in situ oxidation observation at the very initial stage was investigated by high-temperature optical microscopy in air. The
oxide layer of long-term oxidation behavior was examined by scanning electron microscopy (SEM) combined with an energy dispersive X-ray
spectroscopy unit (EDX), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The oxidation kinetics follows a parabolic
rate law. The oxidation rate decreases gradually as the oxidation proceeds. The oxidation of the composite took place firstly on Ti because
of the higher reactivity of Ti and O2 than that of TiC and O2 . However, the TiC reinforcement can decrease the overall oxidation rate at 550,
600, and 650 ◦C. It is attributed to the formation of thin and dense oxidation, the enough strong interface cohesion between reinforcements
and the titanium matrix alloy.
© 2005 Elsevier B.V. All rights reserved.
Keywords: High-temperature; Oxidation; In situ; Titanium matrix composites; Oxidation kinetics
1. Introduction out on in situ TMCs oxidation. It is necessary to investig
您可能关注的文档
- 《MTK_USB数据线刷机驱动安装教程》.doc
- 《Multi-lateral trade negotiations and the Most Favored》.pdf
- 《multinational corporations and trade strcuture》.pdf
- 《Multinational firms technology diffusion and trade》.pdf
- 《MV系列USB2.0工业数字相机开发说明书》.pdf
- 《My Faith Still Holds》.pdf
- 《My Trip To Singapore》.ppt
- 《MySQL-Triggers-Translation-CN》.pdf
- 《MY_DSP_FPGA_USB》.pdf
- 《M_touch_技术》.pdf
文档评论(0)