Welding Guidelines for
Sandvik 2RE69
July 2004
1. Introduction
Sandvik 2RE69 is a fully austenitic stainless steel developed primarily to cope with the severe corrosion
conditions existing in the urea industry. The alloy has excellent resistance to corrosion in ammonium carbamate
and nitric acid. 2RE69 also possess good resistance to intergranular corrosion and pitting corrosion.
2RE69 has good weldability. Suitable welding methods are manual metal arc welding (MMA/SMAW), tungsten
inert gas welding (TIG/GTAW), metal inert gas welding (MIG/GMAW) and submerged-arc welding (SAW) with
wire. For overlay welding with strip electrodes, the electroslag welding process (ESW) or submerged-arc
welding (SAW) with strip can be used. Matching filler metals are recommended in order to obtain a weld metal
with optimum corrosion resistance and mechanical properties. All welding consumables are designated Sandvik
25.22.2.LMn.
Sandvik 25.22.2.LMn weld metal and HAZ have a fully austenitic microstructure. 2RE69 as well as 25.22.2.LMn
filler material have an austenitic solidification mode, which imply that the material is more prone to solidification
cracking than standard austenitic grades such as 304L and 316L. Therefore excessive heat input should be
avoided. Still, compared to many other fully austenitic fillers, 25.22.2.LMn has relatively good resistance to hot
cracking due to high manganese content and low impurity level.
In common with most austenitic stainless steels 2RE69 has high thermal expansion and low thermal
conductivity. Welding must therefore be carried out with thoroughly prepared welding plans in order to minimise
weld distortion.
The structural stability of 2RE69 is good. However, the thermal cycle during welding must be kept under close
control for optimum properties in the weld.
2. Welding consumables
Sandvik welding consumables for 2RE69 have a matching composition to the base material a
您可能关注的文档
最近下载
- DELIXI德力西仪表JKL5CV JKL2CV智能无功功率自动补偿控制器使用说明书 物料号:A0463099500.pdf
- 道路亮化工程项目可行性研究报告.docx
- 幼儿园必备《师德师风培训》-2024鲜版.ppt
- 新北师大版四年级数学上册《认识更大的数》练习题.pdf
- 【西南大学】[机考][0087]《计算机网络》 (3)辅导资料.doc VIP
- 四川327省考行测真题及解析.doc
- (冀教版)八年级生物下册全教案.pdf VIP
- 广东省汕头市2022-2023学年高一下学期期末考试历史试题(解析版).docx
- 专题 事件类记叙文(记叙文阅读)(原卷版).doc VIP
- 颜料红177的制备工艺分析-analysis of preparation technology of pigment red 177.docx
文档评论(0)