大体积防辐射混凝土结构的裂缝控制研究.pdfVIP

Architectural Engineering May 2015, Volume 3, Issue 2, PP.30-35 Study on the Crack Control of Large Volume Concrete for a Radiation Protection Structure Fei Wang Infrastructure Division of the First Affiliated Hospital of Soochow University, Suzhou 215006, China Email: wangfei197908@126.com Abstract For the structure of radiation protection, the crack control of large volume concrete structure is very important. The concrete crack control level is strict because of two factors: the large-volume concrete and radiation protection concrete elements. Based on a specific projects study, this paper took an underground engineering structure as a major radiation source structure to study on the crack control of large volume concrete through construction cracks control calculation and self-constraint crack control, and maintenance during construction and temperature control, all the conclusion can be reference for the similar projects. Keywords: Large Volume Concrete; Radiation; Radiation Protection; Concrete Mix Proportion 大体积防辐射混凝土结构的裂缝控制研究 王斐 苏州大学附属第一医院基建办，江苏 苏州 215006 摘 要：为了确保结构的防辐射，确保大体积混凝土结构的抗裂性十分重要。受大体积混凝土与防辐射混凝土两大因素 的控制，其混凝土裂缝控制要求等级要求严格。本文结合具体工程，开展了一个直线加速器室的重大辐射源所在地下结 构的大体积防辐射混凝土的裂缝控制研究，通过施工前的裂缝控制计算、自约束裂缝控制验算，以及施工过程中的养护 和温度监控，实现裂缝最佳控制，相关结论对于类似工程提供了完整的参照。 关键词：大体积混凝土；放射；防辐射；混凝土配合比 引言 本工程为苏州大学附属第一医院平江分院一期二标段土建工程，地下2 层，地下部分建筑面积约为52000 平方米，地下室楼板、顶板采用的是梁板结构，地下室层高：地下二层：5.05m、5.15m、7.05m （空心板）； 地下一层：4.55m、5.0m。本工程中地下二层直线加速器室顶板厚度为3.2m 、2.9m 、1.3m ，属于重大危险源。 此区域为 19-21 轴L-R 轴之间，约 13.4×45.85m2 左右面积，2.9m 厚板分为2 块，3.2m 厚板分为1 块，其余 为1.3M 厚板，加速区的净高为3.9M 。 医用直线加速器对肿瘤疾病有良好的治疗效果，但如果防护不当，其高能电磁辐射也会给周边人员造成 伤害。为了防止射线的泄漏，除进出治疗室的各种管道和线路均应预留、预埋外，不允许成型后钻孔，更不 能有穿透的施工缝，并要严防大体积混凝土的水化热反应引起的裂缝[1] 。因此，除了应做好原材料的选择和 优化配合比以及各种管道和线路的预留、预埋外，还必须做好对钢筋的绑扎、模板的安装、混凝土施工缝的 位置的留置、混凝土浇筑（原材料的选用、浇筑顺序、浇筑速度、温度控制、保养）都提出了很高的要求[2] 。 该直线加速区混凝土设计强度等级为C35，C45、C60 三个等级，采用中砂、5～25mm 石料、C35，C45 混凝土采用金峰牌P.O42.5 级或南方P.O42.5 普通硅酸盐水泥，C60 采用金峰牌P.O52.5 普通硅酸盐水泥，经 过原材料优选，主要参照 GB50119 －2011 《混凝土外