重防腐用快干高性能水性环氧铁红底漆的研制.docVIP

重防腐用快干高性能水性环氧铁红底漆的研制 施铭德，刘思平，梁基码（武汉铁神化工有限公司，430223） 摘要： 通过对水性环氧树脂和固化剂的选择，结合防锈颜料的作用机理，再配以各种高性能助剂，成功开发了重防腐用快干高性能水性环氧铁红底漆。该漆具有干燥迅速、低温（5℃）施工性良好、高固含、成膜丰满、施工时限长的特点，漆膜具有优异的物理性能，良好的耐盐雾性，其耐盐雾性可达2200小时。在重防腐领域具有广泛的应用前景。 关键词：水性环氧树脂 ； 快干； 耐盐雾性 Heavy anti-corrosion fast drying with high performance waterborne epoxy iron oxide red primer development ShiMingDe, LiuSiPing, LiangJima, ZhouAi (WUHAN FERRO-GUARDIAN CHEMICAL CO., LTD., 430223) Abstract: Based on the choice of waterborne epoxy resin, combined with the antirust pigment mechanism, match again with all kinds of high performance additives, successful development of heavy-duty fast drying with high performance waterborne epoxy iron oxide red primer. The varnish has dry quickly, low temperature (5 ℃) construction good sex, high solid content, film plump, construction time long characteristics, it has good physical properties, and good to salt mist sex, the salt-fog sex can reach 2200 hours. In the heavy anti-corrosion field has a broad prospect of application. Keywords: waterborne epoxy resins; Quick dry; Resistant to salt mist sex 一 引言 随着环保法规的强化，溶剂型涂料受到限制。从而促使涂料向高固体份涂料、水性涂料等环保型涂料的方向发展。尤其以水作溶剂的水性涂料具有节约能源、零VOC排放的优点，日益得到广泛的应用。2010年中国行业资讯大全报告中环氧体系占重防腐体系的30%的比重，而目前环氧体系大多是溶剂型的，随着安全、环保方面的要求，高性能水性环氧体系涂料的开发力度显得尤为迫切。 水性环氧涂料体系对各类底材具有较高的附着力，涂膜具有优异的物理性能和耐化学介质。其以水作为溶剂，价格低廉、环保安全。但目前市面上，由于水性体系在冬季低温施工及湿度太高时其干燥速度较慢的缺陷，在重防腐领域其应用受到一定的限制。而我公司研制的重防腐用快干高性能水性环氧铁红底漆防腐性能优异，固含高、漆膜丰满度好、干燥迅速，低温（5℃）施工性良好，耐盐雾性达2200小时，在市场推广中得到客户的一致好评，该产品具有较强的市场竞争力。 二 实验部分 2.1主要原材料和配方 重防腐用快干高性能水性环氧铁红底漆主要原材料和配方见表1。 表1：重防腐用快干高性能水性环氧铁红底漆主要原材料和配方 组份 材料名称 质量份 材料供应商 A组份 去离子水 8 自制 防锈原料 13.5 德国进口 有机缓蚀剂 1.5 德国进口 分散剂 0.2 BYK 氧化铁红 10 上海一品 水性消泡剂 0.4 EASTMAN 增稠剂 0.3 德国进口 防闪锈剂 0.2 之途化工 基材润湿剂 0.2 BYK 云母粉 2 格锐 填料 10.5 国产 水性环氧乳液 52 自制 水性流平剂 0.2 EASTMAN 附着力增进剂 1 国产 B组份 水性环氧固化剂 7.5 德国氰特化工 去离子水 6.7 自制 2.2 重防腐用快干高性能水性环氧铁红底漆性能测试结果见表2。 表2：重防腐用快干高性能水性环氧铁红底漆性能测试结果 检测项目 检测结果 检测标准 漆膜颜色及外观 铁红色，平