02mm厚GH4169薄片激光微焊接接头的组织性能龚伟怀.pdfVIP

38 6 Vol.38, No.6 2011 6 CHINESE JOURNAL OF LASERS June, 2011 0.2 mm 厚GH4169薄片激光微焊接接头的组织性能 1 1 2 2 1 龚伟怀 陈玉华 吕 榛 李 喆 柯黎明 1, 330063 2 () , 412002 0. 2 mm GH4169 , ,, ,, 12. 8 W, 2. 7 ms, 5.0 Hz , 0.2 mm GH4169 , , ;; GH4169 ; ; TG456.7 A doi : 10. 3788/ CJL201138. 0603008 Microstructure and Properties of 0.2 mm Thick Sheet GH4169 by aser Microwelding 1 1 2 2 1 Gon Weihuai Chen Yuhua LZhen Li Zhe Ke Limin 1 National Defense ey Disciplines Laboratory of Light Alloy Processing Science and Technology , Nanchang Hangkong University , Nanchang, Jiangxi 330063, China 2 China National South Aviation Industry Limited Company , Zhuzhou , Hunan 412002, China Abstract The laser weldin experiments on weld 0. 2 mm thickness of the superalloys GH4169 with microlaser pulse is carried out, the impact of weldin process parameters onj oints formin is analyzed, and the microstructure and properties of joints are studiedby makin use of optical microscopy, electronic precision stretchin machine, and other analysis and detection methods. The results show that usin ar on as a shieldin as, 0. 2 mm thick GH4169 to the laser as heat source can be successful butt weldin with process parameters of the power of 12. 8 W, pulse width of 2. 7 ms, pulse frequency of 5. 0 Hz, and a ood welded appearance is formed, and the joint tensile stren th is hi her than the base metal. The microstructure composed of weldedjoints is small equiaxed rains in the weld center and columnar rains near the fusion