Grain boundary–slip bands interactions Impact on the fatigue crack initiation in a polycrystalline forged Ni-based superalloy》.pdfVIP

Acta Materialia 99 (2015) 325–336 Contents lists available at ScienceDirect Acta Materialia journal homepage: www.elsevier .com/locate/actamat Grain boundary–slip bands interactions: Impact on the fatigue crack initiation in a polycrystalline forged Ni-based superalloy Baptiste Larrouy a,b, Patrick Villechaise a, Jonathan Cormier a,⇑, Olivier Berteaux b a Institut Pprime, CNRS – ENSMA – Université de Poitiers, UPR CNRS 3346, Physics and Mechanics of Materials Department, ISAE-ENSMA – Téléport 2, 1 avenue Clément Ader, BP 40109, 86961 Futuroscope Chasseneuil Cedex, France b Turbomeca – SAFRAN Group, Materials, Processes and Expertises Department, 64511 Bordes Cedex, France a r t i c l e i n f o a b s t r a c t Article history: 0 Low cycle fatigue properties of polycrystalline c–c Ni-based superalloys are dependent on many factors Received 11 June 2015 such as temperature, environment, grain size and distribution of the strengthening phases. Under LCF Revised 4 August 2015 conditions, an intergranular crack initiation is often observed. The local conditions favoring such a dam- Accepted 5 August 2015 TM age mode are analyzed in this paper considering the high strength cast and wrought Udimet 720Li alloy Available online 26 Aug