深冲板 St15 再结晶退火织构演变的计算机模拟 孙景宏，刘雅政，周乐育 （北京科技大学材料科学与工程学院，北京 100083 ） 摘要：运用二维元胞自动机方法，以深冲板 St15 热轧、冷轧、退火组织和织构以及再结晶规律实 验结果为初始条件和参照，分别对深冲板再结晶退火过程的再结晶和晶粒长大进行了计算机模拟。 通过模拟，预测了再结晶退火各个阶段组织和织构。得出在700℃恒温超过 10h，晶粒尺寸、形状 和织构都趋于稳定，织构以有利织构组分{111}110和{111}112织构为主。 关键词：元胞自动机，深冲板，织构，模拟 Simulation on Texture Evolution during Recrystallizaiton Annealing of Deep-Drawing Sheet St15 Sun Jinghong, Liu Yazheng, Zhou Leyu (Materials science and engineering school, USTB, Beijing 100083, China) Abstract: Taking hot rolling, cold rolling, annealing microstructure and texture and experiment result of recrystallization rule of deep-drawing sheet st15 as initialization condition and reference, two-dimensional Cellular Automaton methods are used to respectively simulate the recrystallization and grain growth of recrystallization annealing of deep-drawing sheet. By means of computer simulation, microstructures and textures of different period of recrystallization annealing are predicted. Achieve that grain size, shape and texture become stable after constant temperature grain growth at 700℃ for 10 hours, and advantaged texture component {111}110 and {111}112 are dominant. Keywords: Cellular Automaton, Deep-Drawing Sheet, Texture, Simulation 1 前言 有非常广泛的适用性。因而应用CA方法的一个重 要步骤就是确定具有实际物理意义的缺陷系统作 深冲板所要求的良好成形性能，是由其微观 为组成连续体的所谓“基础实体”[1]。 组织结构，尤其是强的有利织构所保证的，而在 2.2 模拟方法初始设定 化学成分一定的情况下，其微观组织结构则依赖 于加工条件和生产工艺。对于微碳铝镇静钢深冲 深冲板St15 再结晶过程是在其冷轧组织上发 板 St15，其生产过程中大压下量冷轧后的再结晶 生的，但由于其罩式退火工艺所要求的缓慢加热， 退火相对来说是得到理想组织与织构的关键工 使得冷轧组织在发生再结晶前已进行了较为完全 序。以深冲板组织和织构演变的实验研究为基础， 的回复，所以实际上深冲板再结晶是