《挤压力对真空吸渗挤压制备2DCfAl复合材料的影响(英文期刊)》.pdfVIP

Trans. Nonferrous Met. Soc. China 23(2013) 1915−1921 Effect of specific pressure on fabrication of 2D-C /Al composite by vacuum and pressure infiltration f 1 1,2 1 1,2 1 Yu-qin MA , Le-hua QI , Wu-qiang ZHENG , Ji-ming ZHOU , Lu-yan JU 1. School of Mechanical Engineering, Northwestern Polytechnical University, Xi’an 710072, China; 2. Key Laboratory of Contemporary Design and Integrated Manufacturing Technology of Ministry of Education, Northwestern Polytechnical University, Xi’an 710072, China Received 30 January 2013; accepted 6 May 2013 Abstract: Carbon fiber reinforced aluminum matrix (C /Al) composite has many excellent properties, and it has received more and f more attention. Two-dimensional (2D) C /Al composites were fabricated by vacuum and pressure infiltration, which was an f integrated technique and could provide high vacuum and high infiltration pressure. The effect of specific pressure on the infiltration quality of the obtained composites was comparatively evaluated through microstructure observation. The experimental results show that satisfied Cf/Al composites could be fabricated at the specific pressure of 75 MPa. In this case, the preform was infiltrated much more completely by aluminum alloy liquid, and the residual porosity was seldom found. It is found that the ultimate tensile strength of the obtained C /Al composite reached maximum at the specific pressure of 75 MPa, which was improved by