《大塑性变形6013铝合金的时效特性与力学性能（英文版）》.pdfVIP

Trans. Nonferrous Met. Soc. China 24(2014) 3858−3865 Aging behavior and mechanical properties of 6013 aluminum alloy processed by severe plastic deformation Man-ping LIU1 1 1 1 1 , Ting-hui JIANG , Jun WANG , Qiang LIU , Zhen-jie WU , Ying-da YU2 2 2,3 , Pål C. SKARET , Hans J. ROVEN 1. School of Materials Science and Engineering, Jiangsu Province Key Laboratory of Materials Tribology, Jiangsu University, Zhenjiang 212013, China; 2. Department of Materials Science and Engineering, Norwegian University of Science and Technology, Trondheim 7491, Norway; 3. Center for Advanced Materials, Qatar University, P.O. Box 2713, Doha, Qatar Received 17 October 2013; accepted 7 November 2014 Abstract: Structural features, aging behavior, precipitation kinetics and mechanical properties of a 6013 Al–Mg–Si aluminum alloy subjected to equal channel angular pressing (ECAP) at different temperatures were comparatively investigated with that in conventional static aging by quantitative X-ray diffraction (XRD) measurements, differential scanning calorimetry (DSC) and tensile tests. Average grain sizes measured by XRD are in the range of 66−112 nm while the average dislocation density is in the range of 1.20×1014 14 −2 −1.70×10 m in the deformed alloy. The DSC analysis reveals that the precipitation kinetics in the deformed al