《大塑性变形镁合金的晶粒细化（英文版）》.pdfVIP

Trans. Nonferrous Met. Soc. China 24(2014) 3747−3754 Grain refinement of magnesium alloys processed by severe plastic deformation Yong-jun CHEN 1,2,3 1 4 5 2 2,6 , Qu-dong WANG , Jin-bao LIN , Man-ping LIU , Jarle HJELEN , Hans J. ROVEN 1. National Engineering Research Center of Light Alloy Net Forming, Shanghai Jiao Tong University, Shanghai 200030, China; 2. Department of Materials Science and Engineering, Norwegian University of Science and Technology, Trondheim 7491, Norway; 3. ERC for Revolutionizing Metallic Biomaterials, North Carolina AT State University, Greensboro, NC 27411, USA; 4. School of Applied Science, Taiyuan University of Science and Technology, Taiyuan 030024, China; 5. School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, China; 6. Center for Advanced Materials, Qatar University, Doha POB 2713, Qatar Received 17 October 2013; accepted 22 November 2014 Abstract: Grain refinement of AZ31 Mg alloy during cyclic extrusion compression (CEC) at 225−400 °C was investigated quantitatively by electron backscattering diffraction (EBSD). Results show that an ultrafine grained microstructure of AZ31 alloy is obtained only after 3 passes of CEC at 225 °C. The mean misorientation and the fraction of high angle grain boundaries (HAGBs) increase gradually by lowering extrusion temperature. Only a small fraction of twinning is observed by EBSD in AZ31 Mg