钢材控轧和控冷技术的发展 [摘要控轧控冷是对热轧钢材进行组织性能控制的技术手段，目前已经广泛应用于热轧带钢、中厚板、型钢、棒线材和钢管等钢材生产的各个领域。阐述了控轧控冷工艺的机理和工艺特点，介绍了为改善板形而开发的分开的冷却和润滑系统以及动态轧制工艺、GCr15轴承钢控轧新工艺的热模拟实验结果和低碳贝氏体钢的新发展。指出应积极消化吸收先进的控轧控冷工艺，研制开发出高强、高韧性钢板。控控冷低碳贝氏体钢应变诱导 M,aterial?Forming?and?Control?Engineering12? Abstract:?Controlled?rolling?rolling?and?control?cooling?is?microstructures?and?properties?of?hot?rolled?steel?control?technology,?has?been?widely?used?in?the?hot?rolled?strip?steel,?plate,?steel,?wire?rod?and?steel?pipe?and?other?steel?products?production?fields.?This?paper?expounds?the?control?mechanism?and?process?characteristics?of?cold?rolling?process,?is?introduced?to?improve?the?strip?shape?and?development?of?the?separate?cooling?and?lubrication?system?as?well?as?the?dynamic?rolling?technology,?the?new?technology?of?GCr15?bearing?steel?controlled?rolling?hot?simulation?experiment?results?and?the?new?development?of?low?carbon?bainite?steel.?Points?out?that?should?actively?absorb?advanced?controlled?rolling?process?of?controlled?cooling,?developed?high?strength?and?high?toughness?steel?plate. Keywords:??Controlled?rolling;?Control?of?cold?rolling;?Low?carbon?bainite?steel;?Strain?induced 1.引言制轧制和控制冷却技术是20世纪60~70年代发展起来的热机械处理或形变热处理技术。控制轧制和控制冷却技术代表了高强度低合金钢的发展方向。控轧控冷是一种定量的按预定程序控制热轧钢形变温度、压下量(形变量)、形变道次、形变间歇停留时间、终轧温度以及终轧后的冷却速率、终冷温度、卷取温度等参数的轧制工艺。通过降低终轧温度的方法来改善钢的力学性能,早在20世纪30年代已为人注意。1925年H.Hanemann和F.Lucke发现,通过降低最终热加工的变形温度可使晶粒细化,从而提高轧制产品的力学性能。然而,由于低温轧制的较大轧制负荷使一般轧机难以承受,因而这项技术很长时间并未在工业上得到实际应用。20世纪50年代,采用控制轧制生产出352MPa级别的C-Mn钢,是世界上首次采用TMCP工艺进行的商业性生产。直至60年代,人们认识到Nb对奥氏体再结晶的强烈阻止作用,可使钢在相对高的温度下控轧,这项技术才开始得到广泛的注意和应用。60年代中期英国的钢铁研究人员对控制轧制开始进行了系统的研究,之后日本和法国的科研人员也相继进行了深入的探索和开发。他们的研究成果为开发现有的控轧控冷状态的高强度钢种提供了基础 2.我国控制轧制、控制冷却技术的发展我国有丰富的铌、钒、钛和稀土资源，具有发展微合金控制轧制、控制冷却技术的广阔前途。近十年来，尤其是第六个五年计划期间以来，控制轧制、控制冷却技术在我国取得了不小的进展。目前每年采用控制轧制、控制冷却工艺生产的刚才已经超过100万吨，涉及到20多个钢种，已经应用到造船、石油、天然气输送管线、锅炉及压力容器、钢板桩、汽车大量、螺纹钢筋、钢丝绳、轴承及地质管等方面。其中板材占40%左右，棒、线材占60%左右，管材和型材所占比例较小。目前控制轧制、控制冷却技术在工业试验和生产上的应用如表1-1所示。国内各厂采用控制轧制和控制冷却工艺在提纲产品综合性能方面所获得的效果上2350