大体积混凝土裂缝分析处理.docVIP

大体积混凝土裂缝分析处理 　　摘要：随着建筑规模的逐渐增大，大体积混凝土施工变得更为多见。由于受施工材料、施工技术、外部环境等多方面的影响，混凝土裂缝较易出现，直接影响建筑物的使用性能。因此，施工队伍必须不断提高施工预控技术，减少裂缝出现，对于已经出现的裂缝应当及时察觉，并采取处理措施，从而保障建筑质量。本文分析了大体积混凝土裂缝的出现原因，并介绍了预防、检查和处理裂缝的技术。 　　关键词：大体积混凝土；裂缝；成因；预控;处理 　　Abstract: with the construction scale is gradually increased, the mass concrete construction become more rare. Due to construction materials, construction technology, the influence of external environment and other aspects, the concrete crack appears more easily and directly influence on the performance of the building use. Precontrol construction team, therefore, must constantly improve the construction technology, reduce the cracks appeared, to have cracks shall timely notice, and take measures, to ensure construction quality. This article analyzed the reasons of the cracking of mass concrete, and introduces prevention technology, check and deal with the crack. 　　Key words: mass concrete; Fracture; Genesis; Preview; To deal with 　　中图分类号：TU755文献标识码：A文章编号：2095-2104(2013) 　　前言 　　任何现浇混凝土，其尺寸到达必须解决水化热及随之引起的体积变形问题，即最大限度减少开裂影响的，或建筑物的基础最小边尺寸在1～3m范围内就属于大体积混凝土。裂缝是大体积混凝土结构的严重病害。混凝土早期表面裂缝在气温骤降形成的温度应力和外力的作用下，会发展成为具有破坏性的贯穿逢和深层裂缝。贯穿裂缝和深层裂缝会破坏结构的整体性，改变混凝土的受力条件，有使局部甚至整体结构发生破坏的可能，严重影响构造物的质量和运行安全性。而大体积混凝土往往运用在一些重要的结构上，一旦出现裂缝，可能造成的损失会更加严重，因此必须做好大体积混凝土的预控施工。 　　 　　一、大体积混凝土裂缝成因 　　混凝土裂缝产生的原因有很多种，主要因素是温度和湿度的变化、结构不合理、混凝土的脆性和不均匀性、不合格的原材料及添加剂、模板变形和基础不均匀沉降等。 　　1、温度因素 　　混凝土在硬化期间水泥产生大量水化热，内部温度不断上升，在混凝土表面引起拉应力。后期在降温过程中，由于受到基础或老混凝土的约束，又会在混凝土内部出现拉应力。气温的降低也会在混凝土表面引起很大的拉应力，当混凝土的内部拉应力超出混凝土的抗裂能力时，即会出现裂缝。 　　2、水分因素 　　配制混凝土时主要是水泥、砂石等原材料与水分之间的搭配。在混凝土的拌和用水中，只需要消耗约20％的水分，而剩余的水分全部会被蒸发。水分蒸发也是引起裂缝出现的一大因素，这些收缩变形引起的裂缝较为多见，对于混凝土使用性能的影响也是比较大的 　　3、浇注因素 　　混凝土在浇注过程中会受到温度的变化影响，很容易在内部形成膨胀变形现象，膨胀造成地基内部的应力增大，致使混凝土结构变形问题更加严重，导致混凝土内部承载过大而引起裂缝。 　　二、大体积混凝土裂缝的预防措施 　　（一）降低水泥水化热和变形 　　选用低水化热或中水化热的水泥品种配置混凝土，如矿渣硅酸盐水泥、火山灰质硅酸盐水泥、粉煤灰水泥、复合水泥等。充分利用混凝土的后期强度，减少每立方米混凝土中水泥用量。根据试验每增减10kg水泥，其水化热将使混凝土的温度相应升降1℃。使用粗骨料，尽量选用粒径较大、级配良好的粗骨料；控制砂石含泥量；掺加粉煤灰等掺合料和相应的减水剂、缓凝剂，改善和易性、降低水灰比，以达到减少水泥用量、降低水花热的目的。在基础内部预埋冷却水管，通入循