干法脱硫灰在混凝土中的应用探索 文蓓蓓 武汉武新新型建材有限公司，湖北武汉 430080 摘 要：十八大报告把环境保护、资源节约、能源节约、发展可再生能源、水、大气、土壤污染治理等等一系列事项统一为“生态文明”的概念，环境保护得到了前所未有的关注。而控制钢厂及烧结厂SO2的排放已成为降低中国SO2排放总量的重要措施[1],随之而产生的大量脱硫灰的综合利用亦成为亟待解决的问题.本文通过对干法脱硫灰的物理、化学性质的分析，研究了其对混凝土强度、凝结时间、安定性的影响。 关键词：干法脱硫灰 矿粉 混凝土 安定性 Dry desulfurization ash in concrete application exploration WUXIN MATERIALS COMPANY LIMITED WENBEIBEI Abstract:The eighteenth big report of environmental protection, resource conservation, energy conservation, development of renewable energy, water, air and soil pollution and so on a series of items for unity \ecological civilization\ concept, environmental protection is under unprecedented attention. And control steel plant and sintering plant SO2 emissions has become lower the SO2 emission of the important measures, and with it the produce of the comprehensive utilization of desulfurization ash has become a urgent problem to be solved. This article through to dry desulfurization ash of physical and chemical properties of the analysis, the research on concrete strength, setting time, the influence of stability. Keywords: Dry Desulfurization Ash, GGBS, Concrete, Stability 0引言 随着环保意识的增强，国家对污染源的控制不断强化，越来越多的烧结厂等采用了不同的烟气脱硫装置，与此同时排放出大量的脱硫灰。常用的脱硫工艺主要有湿法脱硫和干法脱硫两种。湿法脱硫工艺是将水和石灰配制成浓度为35~50的浆液或将水直接喷入烟气中以降低烟气温度，形成必要的反应条件。 NID脱硫工艺。NID技术以生石灰或消石灰作为吸收剂,与除尘器捕集下来的具有一定碱性的循环飞灰混合增湿后注入反应器,使之均匀地分布于热态烟气中。此时,吸收剂表面水分被蒸发,烟气得到冷却,但湿度增加,烟气中的SO2、HC等酸性组分被吸收生成CaSO3·1/2H2O和CaCl2·4H2O。被除尘器捕集下来的脱硫终产物和未反应完全的吸收剂再部分注入混合增湿装置,并补充新鲜吸收剂后进行再循环从而大大提高了吸收剂的利用率。 1试验材料和方法 1.1 试验材料 脱硫灰来源武钢烧结厂，采取NID脱硫工艺，其外观为微黄干粉状，筛余为13.2%，其化学成分见表1-1。 武新矿粉S95级，其化学成分见表1-2。 武汉亚东P.O42.5水泥，其化学成分见表1-3。 标准砂：符合中国ISO标准砂的质量要求。 表1-1干法脱硫灰化学分析（%） Loss SiO2 Al2O3 Fe2O3 CaO MgO f-Cao CLˉ SO32- SO42- 18.62 1.09 0.76 0.48 51.91 1.14 17.9 1.022 18.22 8.88 表1-2武新矿粉S95级化学分析 Loss SiO2 Al2O3 Fe2O3 CaO MgO SO3 CLˉ 0.20 34.19 14.72 0.27 39.76 6.95 1.96 0.010 表1-3武汉亚东P.O42.5水泥化学分析 Loss SiO2 AL2O3 Fe2O3 CaO MgO SO3 CLˉ f-Cao 2.7 21.67 4.95 3.47 64.44 3.30 24.8 0.002 0.92 1.2 试验方法： 标准稠