聚烯烃与氟树脂共混物的制备-毕业论文.docVIP

毕业论文 题 目 及性能表征 学 院 专 业 班 级 学 生 学 号 指导教师 二〇一四年月日摘 要 本论文用双螺杆挤出机，将聚乳酸（PLA）与乙烯-四氟乙烯共聚物（ETFE，俗称F40）分别按质量比为1/99、3/97和5/95进行共混改性，熔融挤出制备PLA/ETFE共混物，经过切粒和干燥，制备了一系列的PLA/ETFE物理共混试样。然后对不同质量比的共混试样进行了一系列的性能表征。通过差示扫描量热仪（DSC）分析不同比例试样中两种原料的相容性；通过差热-热重分析仪ABSTRACT In this paper, we used a twin-screw extruder to prepare a series of PLA/ETFE physical blending sample through melting, cutting and drying, according to the weight ratio of 1/99, 3/97, 5/95. And then, we conduct a series of the characterizations of the different samples. Analyse the thermal stability of the blends by DSC. Through the TGA analyzed the quality change with increasing temperature of different samples. The melt viscosity of the samples which were of different proportions were measured by of melt indexer. We observed the morphology of the different samples’ section and surface by SEM. Through the research we can conclude that: with the increase of PLA in PLA/ETFE , the blends do not change a lot, PLA always exist in blends with the form of discrete particles, and the compatibility of them is poor, but mixed evenly and it is easily molding. Key words: Blending; ETFE; PLA; Characterization 目 录 摘 要 - 1 - ABSTRACT - 2 - 1 前言 - 4 - 1.1 国内外含氟聚合物的概况 - 4 - 1.2 乙烯-四氟乙烯共聚物（ETFE） - 4 - 1.2.1 乙烯-四氟乙烯共聚物（ETFE）的简介及基本性能 - 4 - 1.2.2 乙烯-四氟乙烯共聚物（ETFE）的制备 - 4 - 1.2.3 乙烯-四氟乙烯共聚物（ETFE）的改性 - 5 - 1.2.4 乙烯-四氟乙烯共聚物（ETFE）的应用 - 5 - 1.3 聚乳酸（PLA） - 5 - 1.3.1 聚乳酸（PLA）的结构 - 5 - 1.3.2 聚乳酸（PLA）的性质 - 6 - 1.3.3 聚乳酸（PLA）的制备 - 6 - 1.3.4 聚乳酸（PLA）的改性 - 7 - 1.3.5 聚乳酸（PLA）的应用 - 7 - 1.4 共混改性 - 8 - 1.5 双螺杆挤出机 - 8 - 1.6 选题的意义与目的 - 9 - 2 实验部分 - 10 - 2.1 主要原料 - 10 - 2.2 主要设备与仪器 - 10 - 2.3 实验方法 - 10 - 2.3.1 选则最佳的加工温度 - 10 - 2.3.2 PLA/ETFE共混物挤出造粒 - 10 - 2.3.3 PLA/ETFE共混物的熔融指数测定 - 11 - 2.3.4 PLA/ETFE共混物的DSC测试 - 11 - 2.3.5 PLA/ETFE共混物的TGA测试 - 11 - 2.3.6 PLA/ETFE共混物的耐碱性 - 11 - 2.3.7 PLA/ETFE共混物的SEM观察 - 11 - 3 结果与讨论 - 12 - 3.1 最