从废旧锂电池中分离回收钴的工艺研究大学生学位论文.docVIP

南京大学 从废旧锂电池中分离回收钴的工艺研究 学院名称： 化学与环境工程学院 专 业： 班 级： 学 号： 姓 名： 指导教师姓名： 指导教师职称： 二〇一三 年 六 月  从废旧锂电池中分离回收钴的工艺研究 摘要 H2SO4溶液为介质,以硫代硫酸钠固体为还原剂,于80 ℃搅拌2.5 h ,溶解锂离子电池中的LiCoO2’ 溶解液中的Li+ 和Co2+ 用NaOH溶液为沉淀剂进行分离; Co (OH) 2沉淀先经过提纯,提纯后的试样在800 ℃下煅烧4 h ,可回收得到Co3O4。Co的纯度达到91.23 %。母液中Li+加固体Na2CO3处理,沉淀后重结晶,得到Li2CO3。Li的纯度达93.5 %。 关键词：锂离子电池; 钴酸锂; 硫代硫酸钠; 回收; 浸出  Research of recycling cobalt from the waste Lithium-ion batteries Abstract: Disposal of spent lithium-ion batteries(LIBS) has becoming more and more important with the growth of production and use of LIBS. Recycling treatment has attracted more and more attentions. Compared to other methods of treatment, recycling can not only resolves environmental problems, but also slows the lack of resource effectively by recovering and reusing of valued metals from LIBS. This project study the craft from the waste separation and recovery of cobalt in lithium battery.The process of dissolving LiCoO2 in Li-ion battery made by Na2S2O3 solution under 80 ℃milled for 2.5 h with H2SO4 solution was studied. The separation of Li+ and Co2+ in solution could be realized by adopting NaOH solution as precipitator , Co3O4 was obtained after Co (OH) 2 had been purified and calcined for 4h under 800℃, its purity was 94.2 %. The Li+ in pregnant liquor was concentrated by adding solid Na2CO3 and Li2CO3 was collected after serious of crystallization, the purity was 93.5 %. Key words: Li-ion battery ; LiCoO2 ; Na2S2O3 ; recovery ; leach  目 录 1.1 研究本课题的意义和目的 1 1.2 国内外本领域科技创新发展概况和最新发展趋势 1 1.2.1锂离子电池的发展概况 1 1.2.2 锂离子电池的结构及材料组成 2 1.2.3 废锂离子电池回收利用的必要性 3 1.2.4 国家相关法规政策 5 1.2.5废锂离子电池资源化技术 5 1.2.6 电极材料的浸出 9 1.2.7 浸出液中金属的提取和分离 9 1.3 废锂离子电池中金属回收研究开发现状的国内外比较 13 1.3.1 废锂离子电池重金属回收研究开发现状 13 1.3.2 国内外技术比较 14 1.4 本课题的研究内容和方案 15