专题汉钢转炉冶炼品种钢的建议_new_new重点解读.docxVIP

专题 汉钢转炉冶炼品种钢的建议 崔征 （ 西安建筑科技大学 西安 710055 ） 摘 要：基于汉钢现状，并考虑国内整体形势的前提下，为达到利益最大化，使其增加利润，对汉钢转炉冶炼品种钢提出相应的建议。在不增加汉钢新的炼钢设备的前提下，参考现有的成熟技术，借鉴有相似工艺钢厂的生产实践经验，汉钢可以对轴承钢GCr15和齿轮钢20CrMnTiH进行试生产。 关键词：汉钢，转炉，轴承钢GCr15，齿轮钢20CrMnTiH Recommendations?of?the?Shanxi?Han?steel?Group?Corporation smelting?steel Cui zheng （Xi’an University of Architecture and Technology Xi’an 710055） Abstract: Based on?the?present situation of Shanxi Han steel Group Corporation . And?taking into account?the?overall?situation?of?the?premise. To achieve?the?maximum?benefit,the maxim- um?benefit,?which?increases?profits,?Chinesesteel?smelting?quality?steel?to?make ?recommend-ations?accordingly .Without?increasing?Chinese?steel?under?the?condition?of??new steel-making equipment.Reference existing?mature technologies,using?similar?technology steel mill?produc-tion experience. Han steel GCr15?bearing?steel?and?steel?20CrMnTiH?gears?can betested. Key words: Han steel,converter,bearing?steel GCr15?,Gear?steel 20CrMnTiH 中国钢铁行业经过几十年的发展，钢铁产量和质量都有很大的提高。但近几年来，中国钢铁市场低迷，钢价连续下跌，相对于历史最高点跌幅达到44.91%。面对整体低迷的现状，钢铁行业正在积极转型以渡过难关。 1 汉钢现状 汉钢产品简介 陕西汉中钢铁集团有限公司目前年产铁精矿45万吨、生铁150万吨、连铸钢坯200万吨、热轧带钢80万吨、铁合金5万吨、二级冶金焦60万吨、发电1.5亿度、粗苯6000吨、硫铵5000吨、水泥30万吨的生产规模。其中炼钢车间主要生产螺纹钢（分别为HRB335,HRB400,HRB500三个型号），连铸钢坯（主要为150mm×150mm,160mm×160mm两种规格的方坯）和线材（主要生产?5.0mm~22m的光面线材和?6.0mm~16mm的螺纹钢线材盘卷）。 1.2汉钢炼钢车间主要生产设备 1.2.1 车间主要冶炼工艺设备见表1 表1 车间主要冶炼工艺设备表 工艺设备名称设备数量备注KR铁水脱硫装置1套预留1套转炉2座预留1座在线吹氩喂丝站2套预留1套LF精炼炉1套预留1套RH真空处理装置-预留1套1.2.2 主要设备的工艺参数  = 1 \* GB3 ① 脱硫装置主要参数： 脱硫方式 KR法 套数 1套 平均处理量 139.2t 平均处理周期 38min 处理后硫含量 0.010～0.002%  = 2 \* GB3 ② 转炉主要参数： 转炉型式 顶底复吹 转炉座数 2座 公称容量120t 平均出钢量145t 转炉平均冶炼周期 38min  = 3 \* GB3 ③ 在线吹氩喂丝站主要参数： 数量 2座 平均处理周期 12min  = 4 \* GB3 ④ LF精炼炉主要参数： 型式 双钢水罐车、电极横臂旋转式 数量 1座 公称容量 120t 平均处理量 145t 变压器额定容量 25MVA 平均升温速度 4℃/min 平均处理周期 38min 2汉钢转炉冶炼品种钢的建议 由于现在汉钢的产品大纲主要以螺纹钢（分别为HRB335,HRB400,HRB500三个型号），连铸钢坯（主要为150mm×150mm,160mm×160mm两种规格的方坯）和线材（主要生产?5.0mm~2