聚合物结构与性能要点讲解.ppt

snowflake Morphology of PEO in PEO/PMMA blend. Optical micrograph of morphologies observed in a 50/50 samples: (a) Dendrite (D90)—PMMA16, Tx = 58 C, (b) Dense-Branched Morphology (DBM)—PMMA101, Tx = 50 C, (c) Stacked Needles (SN)—PMMA101, Tx = 42 C, (d) Needles (N)—PMM101, Tx = 40 C (J Mater Sci (2007) 42:4521–4529) Electron Microscopy Images of Nylon 6 6 isothermally crystallized from glycerine at different temperatures (30 April, 2002, Tss=2000C) Tc=1450C, 17Kx Tc=1450C, 13Kx Tc=1450C, 46Kx Tc=125, 22Kx Tc=1350C, 22Kx Tc=1250C, 46Kx TEM images of Nylon 6 6 crystallized isothermally at 1200C in 4,4-butanediol solution and then annealing at 1600C for 18 hours. Magnification: 46K 第三章 高聚物的晶态结构 Structure and morphology of crystalline polymers 3.1 聚集态结构概述(Introduction to aggregates) 3.2 高分子结晶特点(special features of polymer crystals) 3.3 高聚物的结晶形态(morphology of polymer crystalline) 3.4 结晶高聚物的结构模型(structure models of crystalline polymers) 3.5 高聚物的结构与X-射线衍射图的关系 (Relationship between structure and X-ray pattern) 3.4 结晶高聚物的结构模型(structure models of crystalline polymers) 高聚物的结构包括晶区结构和非晶区结构。本节所谓的高聚物的结构模型是根据实验事实对晶区和非晶区本身的排列方式，以及晶区和非晶区之间的连接方式提出的假象结构。 应该指出，尽管有实用价值的纤维已经生产了半个世纪之久，但纤维的结构仍处于研究阶段。提出的每种结构模型都是对特定的高聚物，在特定的研究条件下提出的，因此很少具有普遍意义，本节就几种典型的结构模型作一介绍。 3.4 structure models of crystalline polymers 3.4.1缨状胶束模型 (缨状微胞模型)(fringed-micelle model) 1930年， Herrmann基于对纤维素的研究，把Gerngross等人最初对明胶提出的缨状胶束(缨状微胞)转用于纤维素。后来逐渐推广于描述普通高聚物的结构。示意图如下： 3.4 Structure models of crystalline polymers 3.4.1 Fringed-micelle model 3.4 Structure models of crystalline polymers 3.4.1 Fringed-micelle model 特点： (1) 高聚物的结构由结晶和非晶两相组成(两相结构模型); (2) 晶粒有一定的大小和尺寸； (3) 每一个晶粒有许多分子束聚集而成； (4) 每个高分子链可以同时贯穿几个晶区和非晶区。 3.4 Structure models of crystalline polymers 3.4.1 Fringed-micelle model 可解释如下事实： (1) 晶粒尺寸远小于分子链长度； (2) X-射线衍射图中， 既有反映晶区存在的衍射环，又有反映非晶区存在的散射晕圈； (3) 纤维的宏观密度比由晶胞计算的密度小， 又比其完全无定形材料的密度大； (4) 纤维一般可以拉伸许多倍，拉伸后又有回缩的倾向； (5) 拉伸后X-射线的衍射图由衍射环蜕变为弧形衍射斑点。等 Figure 2: Two dimensional repre