蠕墨铸铁生产工艺控制 摘　要：以Z14号生铁为原料，用中频炉熔炼原铁液，加入1.1%的FeSiMg4Re17作为蠕化剂，1%的FeSi75作为孕育剂，采用平底包冲入法蠕化处理原铁液，控制出铁温度为1420～1450，待反应结束后在10min内浇注完毕，可获得合格的蠕墨铸铁工件。检测表明，所生产的铸件成分稳定，石墨蠕化率为62%，机械性能达到国家标准。 Abstract： With Z14 pig iron as raw material, medium-frequency furnace as the smelting device, adding 1.1% FeSiMg4Re17 as vermicular agents and 1% FeSi75 as inoculants, through vermicularizing treatment and inoculation in flat bottom ladle, controlling the smelting iron temperature within 1420～1450 and finishing the pouring within 10 minutes after the reaction, eligible vermicular graphite cast iron pieces are obtained