水性环氧云铁防锈漆中涂漆简述.docVIP

Intended Uses 用途 可作为与富锌底漆配套的高性能水性防锈中间漆，也可单独作为水性漆配套的底漆，还适用于作为金属喷涂层或镀锌层表面的封闭涂层，用于轻度至严重腐蚀环境下的钢结构表面，如船舶、集装箱、海上平台、码头等海洋设施、石油化工管道与储罐、冶金、电力等行业中钢结构件的防锈与防腐。 As a high performance water-miscible anti corrosive intermediate coat according to zinc-rich primer, it can be used to a primer according to water-miscible paint by itself, it can be used to asealer coat on the Surface of the metal, zinc-coated,or steel structure too, it is widely used for the surface of ship, container the platform of the sea, wharf etc…steel structure as the anti corrocsive coat. Product Information产品简介 银灰色，水性双组份环氧云铁防锈漆，含较高颜料体积浓度的r-Fe2O3鳞片状颜料，成膜后能平行定向重叠排列，形成类似“鱼鳞片”的搭接结构，因此具有较高的封闭性和防腐性能良好。 以水为分散介质，不然不爆，可用水稀释和清洗涂装用具，施工过程无污染，具有安全和环保性。 Silvery white, two packages water-miscible M.I.O. epoxy anti-corrosive paint, the volume density of the r-Fe2O3 scale-like pigment is higher, the r-Fe2O3 can be arranged in the dry film of this paint, so the performance of the sealer and anti corrosive is better. It is despersed by water, resist fire and burst, can be diluted or cleaned by water. No pollution, safety and environmental pritection. Application details 产品数据 Volume Solids 固体份 ≥55% Dry Flm Thickness干膜厚度 80 microns equivalent to 145 microns of wet film 80微米相当于145微米湿膜厚 Theoretical Coverage 理论涂布率 3.84m2 /Kg 3.84平方米/公斤 Practical Coverage 实际涂布率 Allow appropriate loss 允许适量损耗 Storage and Handling 施工详述 Mix Radio 混合比 10parts to 1 part(by weight) 重量比 10:1 Method of Application 施工方法 Airless Spray 无空气喷涂 Recommended 推荐采用 Brush or Roller 涂刷或辊涂 Recommended 推荐采用 Conwentional Spray 传统喷涂 Not Recommended 不推荐采用 Thinner 稀释剂 清洁淡水（water））℃ ≤45 ≤24 3hours 小时 Not limit 不限 Storageand Handling 贮存与管理 Storage 贮存 Store in cool and dry conditions（5-40℃） 贮存于5-40℃阴凉干燥环境之中，不得暴露于霜冻环境