负极材料的晶体结构对锂离子电池的影响分析.docVIP

负极材料的晶体结构对锂离子电池的影响 喻佳瑜 （上海工程技术大学 材料工程学院，上海201620） 摘要：锂离子电池在充放电时.锂离子的不断嵌入和脱出极易粉化或者发生相变，在第一次充放电时电极材料表面的活性物质也会和电解液发生反应形成钝化膜，随后会发生锂的合金化团聚，产生体积较大的膨胀与收缩，使电极材料崩溃和脱落，从而影响锂离子电池的电化学性能. 为此，通过对负极材料的改性和给电解液添加些化合物等方法，可以相应增强其电化学性能。 关键词： 锂离子电池；负极材料；晶体结构；电化学性能；改性； The effect of anode material crystal structure on li-ion battery Yu Jiayu (College of Materials Engineering，Shanghai University of Engineering Science，Shanghai 201620，China) Apulverization or phase transformation. In the first cycle of charging-discharging,the electrolyte will take reaction with active material of the surface of anodematieral,it will form a film on the surface of active material. We call it SEI(solid electrolyte impedance). Then it will appear the phenomenon of aggregation and the volume of anode material will expand and shrink. This can make active material exfoliation, which will result in decreasing the electrochemical performance. In order to overcome the problem ,we can improve the performance by modifying the surface of anode material and adding some materials in the electrolyte. Keywords: lithium-ion battery; anode material; crystal structure; electrochemical performance 引言随着全球传统能源储量的日益减少和生态环境的逐步恶化，清洁可再生新能源的开发和应用刻不容缓，其中锂离子电池因其独特的优点在当今的能源结构中起着举足轻重的作用。自从 SONY 公司商业化锂离子电池以来[1]，锂离子电池产业迅猛发展。目前，主要应用于手机、笔记本电脑、摄像机等便携式设备[2]，同时还涉及太阳能和风力发电储能[3]、航空航天、军事、医疗等方面。目前，锂离子电池正向电动汽车领域以及大规模工业储能系统这两个重要的新兴领域发展[4]。 1． 锂离子电池的介绍 锂离子电池主要有五部分构成：正极、负极、电解液、隔膜和固体电解质界面膜。 a. 正极材料 一般选择氧化还原电位较高且在空气中稳定的复合物，目前商业化使用的锂离子电池正极材料按结构主要分为以下三类[5]：①六方层状晶体结构的 LiCoO2(第一代锂离子电池正极材料[6])；②立方尖晶石晶体结构的 LiMn2O4[7]；③正交橄榄石晶体结构的 LiFePO4[8]。 目前，正极材料的主要发展思路是在 LiCoO2、LiMn2O4、LiFePO4等材料的基础上，发展相关的各类衍生材料，通过掺杂、包覆、调整微观结构、控制材料形貌、尺寸分布、比表面积、杂质含量等技术手段来综合提高其比容量、倍率、循环性、压实密度、电化学、化学及热稳定性[5]。 b. 负极材料 目前，商业化广泛使用的锂离子电池负极材料主要分为以下两类：①六方或菱形层状结构的人造石墨[9]和天然改性石墨[10]；②立方尖晶石结构的Li4Ti5O12[11]。 c．