Anti-mold brass engraved chrome craft.docVIP

Anti-mold brass engraved chrome craft The quality of coating adhesion on the main front in the plating process. Plating brief summary: a plating a plating treatment after treatment before plating. Practice has proved that the coating appears shelling, blistering, or even the quality of the accident was not due to plating and other electroplating process per se, but because before plating caused by improper handling and poor. If handled properly before plating on the coating quality plays a very important role, unclean plating surface (oxide film and the oil), even under the most favorable conditions for plating, metal deposition is not uniform, and the combined force will be significantly lower. Therefore, to enhance plating pretreatment, remove oil brass surface, in forming oil (heating water metallographic sandpaper friction) and impurities (pickling degreasing film) process on the basis of increase in reverse electroplating process (anti-engraved) more conducive to the chromium layer adsorption (sulfuric acid wash only copper substrate surface impurities removal, reverse current reverse slot can place the copper matrix depth impurities) advantages of reverse plating process is so attached to the brass surface impurities can not remove surface oil and not fully activate or oxide layer other causes; exposure to crystalline particles, increasing the binding force, lower copper impurity contamination of medicine, and adjust the current density, temperature controlled bath, to find the optimum conditions, improving quality chromium layer . Anti-engraved process: Chromic anhydride 100 ~ 150g / L Sulfate 0.8 ~ 1.2g / L, the optimum value of sulfate 1g / L DW-2015 chrome-plated brass mold additive anti-engraved: 20ml / l Anti-engraved treatment conditions: Temperature 35 ~ 55 ℃ temperature can be maintained midline Current density 20 ~ 50A / Dm2, Third, the time is 1 ~ 4min; Process Washing -DW-2015 copper degreasing agent - washing - activated - w