纳米化处理对锆金腐蚀性能的影响.doc

纳米化处理对锆合金腐蚀性能的影响 石明华1摘 要:腐蚀性能而上述因素中的任何一个因素发生变化，都会导致材料腐蚀性能的改变。因此对于锆合金表面纳米化后腐蚀性能的研究，应该从全方位考虑，从而对锆合金的腐蚀性能有一个全方位的认识。关键词: 表面纳米化 腐蚀 晶界 EFFECTS OF SURFACE NANOCRYSTRALLZATION ON THE CORROSION PROPERTIES OF ZIRCONIUM ALLOYS inghua 1, Zhang Xiyan1、2、3、*, LI Cong3, Liu Nianfu 1, Qiu Shaoyu2, Zhang Qiang3, Zhang Pengchen4,Wei Yiming1 (1. School of Physical Science and Engineering Technology, Guangxi University, Nanning 530004, China; 2. School of Materials Science Engineering , Southwest Jiao tong University, Chengdu 610031, China; 3. National Key Laboratory for Nuclear Fuels and Materials, Nuclear Power Institute of China (NPIC), Chengdu, 610041;） Abstract: This article discussed a superficial nanometer processing to the zircaloy corrosion resistance performance influence. For a surface nanometer and the ultra finer organizations zircaloy, its corrosion property influence factor not only includes the grain size, but also includes the alloy composition, the oxide film organization and the nature, the heat treatment technique, the surface condition, chemistry of reactor coolant, temperature of reactor coolant , heat flux through the cladding, irradiation effects and so on. Any one of these factors change will lead to corrosion property can be change. Therefore, this kind of research should be carried out carefully. Key words: Surface nanocrystallization; Corrosion; Grain boundary 基金项目：国家自然科学基金资助项目 广西自治区研究生创新基金资助项目 作者简介：石明华（1981－），女，硕士研究生 通讯作者：张喜燕，教授；电话：0771－3234302；Email: kehen888@163.com 1.引言 锆及其合金被普遍用于核动力反应堆中作结构部件和燃料包壳,这主要是由于锆具有低的热中子吸收截面,在高温水中有强的抗腐蚀性能和高的机械强度在核反应堆中,由于核燃料的燃耗是核电成本的有效途径,而对于压水堆进一步提高燃耗的主要限制因素是燃料包壳锆合金的水侧腐蚀和吸氢。因此,对锆合金的抗腐蚀性能提出了更高的要求。近几年，随着纳米技术的发展，材料经纳米化后，其机械、物理、化学及电学等方面的性能明显优于普通金属。因此，研究表面纳米化后锆合金的腐蚀性能，揭示其腐蚀机理，2.均匀腐蚀 锆是一种活性金属，其合金在高温水和蒸汽中会发生Zr＋2H2O＝ZrO2+2H2氧化反应。对于锆合金的氧化机理已经作了大量的研究。结果表明，锆合金是良好的电绝缘体，氧化初期，氧化的控制因素主要是由于电子缺陷和空洞。随着氧化膜的增厚，扩散过程起着越来越重要的作用，成为继续氧化的控制因素。研究表明，锆合金的氧化过程，是电子向外迁移，氧通过晶格和晶界向内扩散，在金属－氧化膜界面进行反应，形成具有保护性的氧化膜，当氧化膜厚度达（2-3）μm时，腐蚀速度突然增加，成