毕业设计(论文)-混凝土裂缝控制与成因分析.docVIP

各专业完整优秀毕业论文设计图纸 [摘要]:混凝土作为一种复合型材料，本身具有不连续性，导致混凝土结构出现裂缝。对结构的质量产生影响，降低了结构的适用性和耐久性，更严重的甚至会使结构倒塌破坏。为此，本文拟针对实际工程，着手分析混凝土结构裂缝的产生原因，研究预防混凝土结构裂缝、把裂缝控制在无害的范围内的新技术，探讨混凝土裂缝控制新技术在工程措施中的应用，并在此基础上对混凝土结构裂缝后的安全性作出鉴定。 关键词：混凝土 裂缝 成因 控制 新技术 应用 Abstract:Concrete as a composite material, it has no continuity leads to the expansion of the crack. the cracks will affect the quality of the structure, the applicability and durability, more serious even can make the structure collapse destroyed. For this, in view of the practical engineering, this article is to analyze the reason of the cracking of the concrete structure, the prevention of concrete structure crack, the crack control in harmless in the scope of new technology, discussing the concrete crack control of new technology application in the engineering measures, and to make an identification on this basis to the safety of concrete structure crack. Keywords: Concrete, crack, cause of formation，control ，new technique，apply 目 录 第一章 绪论 1 引言 1 1研究现状 1.1国外研究现状 2 1.2国内研究现状 3 2本文的研究内容与方法 3 3本课题所要达到的目的 4 第二章 混凝土裂缝的分类 5 2.1塑性收缩裂缝 5 2.2温度裂缝 5 2.3沉陷裂缝 6 2.4 干缩裂缝 6 2.5施工操作不当引起的裂缝 7 2.5.1使用离析混凝土 7 2.5.2抢工期拆模早 7 2.5.3砖类成笼上吊成笼堆放 7 第三章混凝土裂缝的成因与危害 3.1裂缝的形成原因 8 3.1.1材料因素 9 3.1.2施工因素 12 3.1.3混凝土养护不当 12 3.1.4施工过程中温度控制不准 13 3.1.5设计原因 14 3.2裂缝影响及其危害 15 3.2.1 混凝土开裂，结构承载能力下降 15 3.2.2 混凝土开裂，结构耐久性能劣化 15 3.3 混凝土开裂的深层原因 16 混凝土裂缝控制新技术 4.1 水分蒸发抑制技术 18 4.2 减缩抗裂技术 20 4.3 水泥水化放热过程的调控 22 4.4 遥爪聚合型增韧技术 23 第五章混凝土裂缝控制新技术在工程实例中的应用 5.1 工程概况 27 5.2 转换层结构设计特征 27 5.3 混凝土配合比设计与原则 27 5.3.1 水泥 28 5.3.2 骨料 28 5.3.3 掺合料 28 5.3.4 膨胀剂 29 5.3.5 外加剂 29 5.4 温度计算及表面裂缝控制 29 5.4.1 混凝土浇筑温度 29 5.4.2 混凝土内部最高绝热温升值 30 5.4.3 混凝土表面最高温度估算 31 5.5 大体积混凝土的施工及养护 5.5.1 混凝土的浇筑 32 5.5.2 混凝土养护保温、保湿及补偿措施 32 5.6 混凝土的温控及实际效果 5.6.1 温度测试 33 5.6.2 混凝土的温控及实际效果 34 5.7 混凝土力学性能及抗渗性能检验结果 34 第六章 结束语 36 展望 37 参考文献 38 致 谢 40  第一章 绪论 引言 随着当前我国建筑业快速发