含針片状粗集料的堆砌性能及对混凝土的影响.docVIP

含针片状粗集料的堆砌性能及对混凝土的影响 摘要：针片状集料堆砌时符合双组分体系的理论堆砌规律。掺入适量针片状颗粒，可增大体系的堆砌度。针片状颗粒堆砌时有很大的机械咬合力，机械咬合力影响混凝土的密实成型， 进而影响混凝土的其他性能。 关键词：针片状 集料 堆砌 混凝土 The stacking properties and the influence to concrete of the aggregate containing elongated and flaky particles Abstract：When be piled up, elongated and flaky particles and non- elongated and flaky particles sysyem is in keeping with the theoretical stacking regularity of two-component system, and appropriate mixture of elongated and flaky particles and non- elongated and flaky particles will be denser. Elongated and flaky particles is closely related to more frictional resistance. More frictional resistance makes compaction of concrete difficult, and then proceed to affect other properties of concrete. Keywords：elongated and flaky particles, aggregate, stackable, concrete 《用石》（G） C M 1.6 X=1 组成 X=0 Y=0 X+Y=1 Y=1 大球 小球 图1 双球堆砌体系的理论堆砌曲线 两种粒径球体的理论堆砌曲线见图1。图中参数及线段的含义： R—大球直径与小球直径之比； C—实验测定的大球理论密堆砌体积； M—实验测定的小球理论密堆砌体积； X，y—大球和小球的体积分数，总体积为1。 横坐标代表大、小球的组成，水平轴表示混合物的组成。 CA—小球加到大球中的浓缩曲线，曲线方程为V=Cx。 MB—大球加到小球中的浓缩曲线，曲线方程为V=x+My。 纵坐标代表相对表观体积（相对表观体积定义为体系的表观体积与真实体积的比值）。当体系固体物料的理论密堆砌度为1时，其相对表观体积为1；当固体物料的相对表观体积为1.6时，其理论密堆砌度为62.5%（单一粒径球体理论密堆砌度为62.5%［1］）X，y—球体和纤维的的体积分数，x+y=1。 SE—较小直径的纤维加入到较大直径的球中填充空隙时的浓缩曲线，直线方程为V=Sx。 FC—大直径的球取代小直径的纤维以及与之相关联的空隙时的浓缩曲线，该直线方程为V=x+Fy。 A—SE和FC的交点，R值无穷大时，纤维填充球间隙的最大理论密堆砌度。 FD—较小直径的球填入到较大直径的纤维之间空隙时的浓缩曲线，直线方程为V=Fy。 SH—用粗纤维取代小球及其相关联的空隙时的浓缩曲线，直线方程为V=y+Sx。 B—FD和SH的交点，为R=0时的最大理论堆砌密度。 从图1看出： 球-纤维的混合可以提高体系的堆砌度。球-纤维堆砌体系中出现了点A、B两个最大理论密堆砌度，两者所对应的球-纤维的组成比例不同，但相对表观体积相同。 纤维加到球中将较快达到最大密堆砌状态； （3） 比较图1、图2，尽管双组分体系的颗粒形状不同，但理论堆砌规律相似。 2 针片状颗粒对集料堆砌的影响 针片状颗粒与非针片状颗粒的组合实际上是一种双组分体系的堆砌问题，应该具有上述双组分体系的堆砌规律。 2.1材料准备 将5~40㎜集料中针