單体结构对混合液晶功耗电流的影响.docVIP

单体结构对混合液晶功耗电流的影响乔云霞，丰景义，史子谦，翟媛媛，贾刚刚(石家庄诚志永华显示材料有限公司，石家庄 050091 qiaoyunxia1980@126.com)摘 要：不同结构单体液晶分别添加到相同混合液晶中，混合液晶的功耗电流与单体结构有很大的相关性。将单体分别添加到基础配方P0中，通过将混晶灌入液晶盒后测试紫外曝光前后的功耗电流，考察了六个系列不同结构单体对混晶功耗电流的影响规律。结果表明加入CCP、CCPA、CCUF单体液晶功耗电流紫外曝光前后比较稳定，CCQUF、CCEP、CCPN类单体液晶由于存在一定的极性紫外曝光前后功耗电流变化较大。关键词：单体液晶；混合液晶；功耗电流；紫外曝光；极性Abstract: The current consumption of Liquid Crystal mixture has great relativity with the monomer structure when add the difference monomers to the same Liquid Crystal mixture. The six series monomers were added respectively to the basic composition P0, and the effect of difference structure monomers to the Liquid Crystal mixture were investigated through test the current consumption of the cell fro-and-aft exposed with UV which were injected with the mixture. The results show that the current consumption is steady for-and-aft exposed with UV after adding monomer CCP or CCPA or CCUF to the Liquid Crystal mixture while the current consumption changed biggish with adding monomer CCQUF,CCEP,CCPN, which had some polarity. Key words: monomer; Liquid Crystal mixture; current consumption; UV exposed; polarityThe Effect of monomers to The Current Consumption of Liquid Crystal MixtureQiao Yunxia，Feng Jingyi，Shi Ziqian，Zhai Yuanyuan，Jia GangGang（Shijiazhuang Chengzhi Yonghua Display Material Co., Ltd, Shi Jia zhuang,050091 qiaoyunxia1980@126.com）1引言信息产业和微电子技术日益发达，人们生活水平不断提高，液晶显示器件也得到了广泛的应用，液晶材料行业的发展也愈来愈广阔，与此同时对液晶显示器的要求也五花八门，日新月异，液晶材料厂也逐渐增多，市场的竞争已经从价格竞争逐渐转移到液晶品质和性能的竞争。提高液晶材料的品质和性能已经被液晶材料行业做为重点项目来抓。本文从液晶混合物灌入液晶盒中后测量功耗电流大小来分析单体液晶化合物的功耗电流的大小，为液晶材料品质的提高提供参考。2实验2.1实验仪器及物品液晶混合物的功耗电流测试时采用7.0微米TN型右旋液晶盒（信利半导体有限公司）。Sartorius Cp224s电子精密天平，北京五洲东方科技发展有限公司；85-2型恒温磁力搅拌器，上海司乐仪器有限公司；P.R.G测试仪，汕尾市城区春生电讯行；DYMAX-5000EC紫外固化仪。本论文所用单体液晶及液晶混合物均为诚志永华材料显示有限公司所生产。2.2单体液晶化合物与母液的配制以下为六个系列单体液晶化合物，见表1表1 六类不同结构单体液晶化合物Table1 Six series monomers with difference structure 单体代码结构式3CCP13CCP32CCUF3CCUF1CCPA3CCQUF3CCEP33CCEP53CCPN5CCPN首先根据以上单体液晶化合物设计母体液晶混合物P0，基础配方的设计主要选用介电常数大，紫外曝光前后功耗电流比较稳定的液晶。P0的组分见表2。然后将上述10