PAGE PAGE 1 大直缝焊管钢板超声波探伤的几种扫查方式浅析 朱吉祥， 王小伍，郭京华 （湖北沙市石油钢管厂 荆州 434001） 摘 要： 本文介绍了大直缝焊管用钢板超声波探伤的三种扫查方式：横向扫查、纵向扫查和摆动扫查，并分别从探头与钢板的相对运动方向、结构、探伤轨迹、探头数量和对探伤机的要求等方面逐一作了分析和比较。 关键词： 钢板 超声波探伤 扫查 横向 纵向 摆动 Analyses to Several UT Scanning Methods to Steel Plate Used by Large Longitudinal Welded Pipe Zhu jixiang ，Wang xiaowu，Guo jinhua (Shashi Steel Pipe Works in Hubei Province,jinzhou ,434001) Abstract: Three types of UT scanning methods of transverse scanning, Longitudinal scanning and swinging scanning to steel plate used by large longitudinal welded pipe are introduced herein. Detailed analyses and comparisons are also made from the aspects such as the relative moving direction between probes and the steel plate, configurations, the inspection traces, the quantity of probes used and requirements to the detector. Key Words: Steel Plate UT Inspection Scanning Transverse Longitudinal Swinging 1.概述 借国家大力开发西部、建设中哈及西气东输等管线的强劲东风，我国大力发展了大口径直缝焊管的生产，弥补了螺旋焊管的不足，使我国的焊管工业又跃上了一个新的台阶。大口径直缝焊管高压输送是石油天然气长输、高压、大流量管道的发展趋势。 大直缝焊管的原料为热轧钢板，板厚6~40mm，板宽655~4500mm，板长8~12.2m。钢板中常见的缺陷有分层、夹渣、裂纹和白点等，其中分层和夹渣是钢板中最为常见的缺陷。超声波法是检测钢板分层缺陷的一种行之有效的方法，在自动扫查时，一般采用水膜脉冲反射式探伤。 2. 扫查 2.1基本概念 在进行超声波探伤时，探伤面上探头与试件的相对运动称为扫查。扫查一般考虑两个原则，一是保证钢板的整个检查区有足够的声束覆盖以避免漏检；二是扫查过程中声束入射方向始终符合标准所规定的要求。 2.2扫查方法与探伤标准 直缝焊管的生产标准很高，国际上公认的和应用最广泛的管线规范有： A．API SPEC 5L（第43版）*； B．ISO3183.1（2；3）[equ GB/T 9711.1（2；3）]*。 国内外许多石油公司在具体的管线建设中都把这两个标准作为基础标准，同时还根据实际需要制定了许多的补充技术规范。这些标准和补充规范都要求钢板必须先进行超声波探伤后才能制成钢管。 由于钢管用途不同，生产钢管的标准各异，钢板超声波探伤执行的标准也就各异，常见的探伤标准有： A．ASTM－A578／A 578M－92*； B．GB／2970.91*； C．SY／T6234.5－1999* D．ZB J74 003－88* 不同的探伤标准决定了扫查方法亦不相同，一般可分为全面扫查、格子线扫查、边缘扫查及列线扫查。 1)．全面扫查：在整个板面上进行全面积（100%）扫查。相邻扫查线之间应有100%的有效波束覆盖。 2)．格子线扫查：在板边缘的一定范围，如50mm以内，作全面积扫查，其余部分划成例如200×200mm的方格子线，探头沿格子线扫查。 3)．边缘扫查：在板材边缘，例如50mm的区域内全面积扫查。 4)．列线扫查：在整个板材的探测面上，沿垂直板的压延方向划出例50或100mm间隔 的直线，探头沿此直线扫查，列线亦可平行压延方向。 将不同的探伤标准与扫查方法作一个分析对照（见表1）： 由表1可知，焊管生产厂家设计、制造钢板超声波探伤设备，首先应灵活而满意地执行国内（外）所有探伤标准，而且还要满足生产节拍（生产节拍一般为4~6分钟/张）。