Polycarbonate has a glass transition temperature of about 147 °C (297?°F),[5] so it softens gradually above this point and flows above about 155 °C (311?°F).[6] Tools must be held at high temperatures, generally above 80 °C (176?°F) to make strain- and stress-free products. Low molecular mass grades are easier to mold than higher grades, but their strength is lower as a result. The toughest grades have the highest molecular mass, but are much more difficult to process. 聚碳酸酯的玻璃化转变温度约147℃下（297°F），[5]，所以它软化逐渐上面这点和流动高于约155°C（311°F），[6]工具必须保持在高温下，一般在80°C（176°F），以应变和应力产品。低分子量等级是比高年级更容易模制，但它们的强度是作为结果