本科毕设论文—电泳沉积纳米tio2陶瓷涂层结构表征与性能研究.docVIP

摘要 电泳沉积法（EPD）制备薄膜具有设备简单，成本低，成膜快，被镀件（用于沉积薄膜的基体）形状不受限制，薄膜厚度均匀，并且其厚度在较大范围内可控等优点。二氧化钛熔点高、化学稳定性好，在复合材料领域具有广阔的应用前景。本文利用电泳沉积法制备出了均匀的二氧化钛薄膜，研究了二氧化钛在悬浮介质中的核电机理；考察了二氧化钛粉末在有机悬浮液中的分散性和稳定性，并且研究了电泳工艺参数对电泳沉积量的影响；特别研究了助剂PEG（聚乙二醇）对电泳膜性能的影响并初步探讨了助剂PEG对二氧化钛膜性能影响的原因；研究了电泳沉积的动力学规律，为今后制备含二氧化钛的层状复合材料打下基础。本文还通过研究了不同烧结温度对二氧化钛晶型的影响定性的表征了光催化性能。 关键词: 电泳沉积 ，二氧化钛膜 ，聚乙二醇 ，Zeta电势 ，烧结 ，光催化 Abstract Film fabricated using electrophoreic deposition(EPD) has the advantages of simpe setup,low cast,time saving,thinkness uniformity,etc. TiO2 has the potential employed as one part of composite because of its high melting point,and excellent chemo-stability.In this paper,homogeneous TiO2 film was produced by EPD.The charged mechanism of TiO2 powder in dispersion medium was studied.The dispersibility of TiO2 powder and stability of TiO2 film was studied.Apart from this,the influence of parameter of deposition was studied；Especially，we studied the influence of film by adding available PEG to it.All of these made it available to fabricate multiplayer composite compound with TiO2 layer.The paper characteristic the performance of photocatalysis by studying the effects of different calcination temperature on crystal phase. Keywords : electrophoretic deposition，TiO2 film，PEG，ZeTa potential，sintering，photocatalysis 毕业设计（论文）原创性声明和使用授权说明 原创性声明 本人郑重承诺：所呈交的毕业设计（论文），是我个人在指导教师的指导下进行的研究工作及取得的成果。尽我所知，除文中特别加以标注和致谢的地方外，不包含其他人或组织已经发表或公布过的研究成果，也不包含我为获得 及其它教育机构的学位或学历而使用过的材料。对本研究提供过帮助和做出过贡献的个人或集体，均已在文中作了明确的说明并表示了谢意。 作 者 签 名：　　 　 　　 日　 期：　　 　 　　 指导教师签名：　　 　 　　 日　　期：　　 　 　　 使用授权说明 本人完全了解安阳工学院关于收集、保存、使用毕业设计（论文）的规定，即：按照学校要求提交毕业设计（论文）的印刷本和电子版本；学校有权保存毕业设计（论文）的印刷本和电子版，并提供目录检索与阅览服务；学校可以采用影印、缩印、数字化或其它复制手段保存论文；在不以赢利为目的前提下，学校可以公布论文的部分或全部内容。 作者签名：　　 　 　　 日　 期：　　 　 　　 目录 摘要 I Abstract I 第一章 绪论 1 1.1引言 1 1.2简介和分类 1 1.2.1电泳沉积简介 1 1.2.2纳米二氧化钛分类及功能 2 1.3纳米二氧化钛国内外应用历程 3 1.4制膜方法简介 4 1.5电泳沉积法制膜技术国内外研究 5 1.6本课题拟解决的主要问题及设计思路 6 第二章 试验条件和方法 7 2.1试验原材料及所用实验仪器 7 2.2 试验方法 7 第三章 试验