《铁水预处理毕业设计》.doc

摘要 采用铁水预处理工艺可以使转炉进行少渣炼钢，使高炉焦比降低，提高了铁水的质量和炼钢厂的经济效益。生产出的含硫含量低的钢材满足了现代科学技术对钢铁材料的要求。所以铁水预处理已成为现代炼钢的重要环节。 本设计对铁水预脱硫的发展历程、现代最常用的铁水预处理的新方法、新工艺、常用的脱硫剂和其反应机理进行了综述，并且在环保方面也进行了综述。本次设计采用的是单喷颗粒镁脱硫的预处理方法。 根据新建年产500万吨合格铸坯炼钢厂的实际工艺流程，比较了几种铁水预处理工艺的优缺点。设计了单喷颗粒镁的脱硫站，并对贮镁仓、喷吹罐、喷射器和喷枪进行了设计和选用。 关键词：铁水预处理；喷镁；脱硫剂；设备参数及布置 Abstract Using iron pretreatment process can make for adoping slagless steelmaking converter, coke reducing furnace, improving the quality of the iron and steel economic benefits. Produce low sulfur also satisfy the steel in modern science and technology for steel materials. So the iron pretreatment has become the important link of the modern steel-making. The design of the development course, gets the most commonly used modern iron pretreatment of new methods, new techniques and common desulfurizer, and the reaction mechanism are reviewed, and in the environmental aspects are reviewed.This design USES is the single particle magnesium injection of desulphurization pretreatment methods. According to the new annual 500 tons of qualified steel casting practical process, compares the advantages and disadvantages of several iron pretreatment process. The design of the single particle magnesium injection, magnesium and desulfurization and blowing cans, injector and spray to carry on the design and selection. Key words ： hot metal pretreatment ；magnesium injection；The desulfurizer；Equipment parameters and layout 目录 摘要 I 第一章 文献综述 1 1.1 前言 1 1.2 铁水预处理的发展历程 2 1.3 铁水预处理的必要性 2 1.3.1 铁水预处理功能演进 3 1.3.2 全量铁水“三脱”处理的效果 4 1.3.3 铁水进行全量预处理的必要性 5 1.4 铁水预处理的方法及比较 8 1.4.1 KR搅拌法 8 1.4.2 KR法脱硫工艺需要注意的问题 10 1.4.3 单颗粒镁铁水深脱硫 11 1.4.4 复合喷吹镁基脱硫剂脱硫 12 1.4.5 KR法与喷吹法的比较 14 1.5 铁水深脱硫的工艺实践 17 1.5.1 原始硫含量及镁粉消耗对深脱硫的影响 17 1.5.2 聚渣剂的优化使用及扒渣效果对铁水深脱硫的影响 18 1.5.3 温度对深脱硫的影响 19 第二章 生产规划 20 2.1 生产规模 20 2.2 产品大纲 20 2.3 产品方案 20 2.4 铁水预处理间的生产计划 21 2.4.1 铁水预脱硫 21 第三章 方案选择 23 3.1 铁水预处理间的位置确定 23 3.2 铁水预脱硫处理方法 23 3.2.1 鱼雷罐车顶喷法（TDS） 23 3.2.2 铁水罐喷吹脱硫 24 3.2.3 混铁车喷粉脱硫 25 3.3 常用的铁水脱硅预处理方