学位论文---年产280万吨冷轧带钢厂工艺设计.docVIP

年产280万吨冷轧带钢厂工艺设计 摘 要 本设计是参考上海宝钢2030mm冷轧厂而进行的冷轧带钢工艺设计，典型产品Q195，1200×0.5mm。 主体设备有浅槽酸洗机组、五机架全连续冷轧机组、罩式退火炉、单机架四滚式平整机组、六段式连续退火机组、横切、纵切及重卷机组、连续电镀锌机组、连续热镀锌机组等。设计产品的品种主要有冷轧钢板、热镀锌板带、电镀锌板带、彩色涂层机组等。掌握了现场生产工艺制度的制定方法、制定了产品方案及金属平衡、确定轧制工艺流程及工艺制度。【】：板带钢，产品方案，全连续轧制，轧机 An annual output of 2.8 million tons cold-rolled strip steel mill process design Abstract The reference design is Shanghai Baosteel 2030mm cold rolling mill and process design for the cold rolled strip steel,a typical product Q195, 1200 × 0.5mm. Shallow groove of the main equipment and pickling line, five-stand continuous rolling mill, hood-type annealing furnace, four roll-formed single rack unit, Six-continuous annealing line, cross-cutting, slitting and recoiling unit, continuous plating zinc unit, continuous hot galvanizing line and so on. Design of the product varieties are cold-rolled steel, hot galvanized strip, galvanized strip, color coated units, etc.. Production process control system on site to develop methods to develop product solutions and metal balance, determine the rolling process and technology system. 【Key words】: steel strip , product programs , completely continuous rolling, mill 1.1 我国冷轧板生产情况 我国现有冷轧薄板生产能力9.87Mt，1999年产量为7.54Mt，2000年产量略有增加。 我国有8套冷连轧机组能力7.56Mt，1999年产量为6.25Mt，基本达到或超过轧机设计能力（宝钢1550、1420mm冷轧新投产），大部分轧机设备利用率超过100%；另有生产硅钢和不锈钢的多辊轧机10套，能力8.25Mt，1999年产量为0.58Mt（张家港和宁波不锈钢生产线新投产），基本达到设计能力；加上11套单机架可逆轧机，能力1.485Mt，1999年产量不到0.8Mt，设备利用率平均约为45%。 1.2 冷轧薄钢板生产的发展历史 钢的冷轧是在19世纪中叶始于德国，当时只能生产宽度20～25mm的冷轧钢带。美国1859年建立了25mm冷轧机，1887年生产出宽度为l50mm的低碳钢带。1880年以后冷轧钢带生产在美国、德国发展很快，产品宽度不断扩大，并逐步建立了附属设备，如剪切、矫直，平整和热处理设备等，产品质量也有了提高。 宽的冷轧薄板(钢带)是在热轧成卷带钢的基础上发展起来的。首先是美国早在1920年第一次成功地轧制出宽带钢，并很快由单机不可逆轧制而跨入单机可逆式轧制。1926年阿姆柯公司巴持勒工厂建成四机架冷连轧机。 原苏联开始冷轧生产是在30年代中期，第一个冷轧车间建在伊里奇冶金工厂，是四辊式，用单张的热轧板作原料1938年在查波罗什工厂开始安装从国外引进的三机架1680mm冷连轧机及1680mm可逆式冷轧机，生产厚度为0.5～2．5mm，宽度为1500mm的钢板。以后为了满足汽车工业的需要，该厂又建立了一台2180mm可逆式冷轧机。1951年原苏联建设了一套2030mm全连续式五机架冷连轧机，年产250万t，安装在新利佩茨克。日本1938年在东洋钢板松下工厂安装了第一台可逆式冷轧机，开始冷轧薄板的生产。1940年在新日铁广坝厂