高铁赤泥制备铁精粉工艺试验 高建阳 （山东淄博 255065，中国铝业山东分公司Research of sorting of fine iron from High-iron red mud Gao Jian Yang （The Research Institute of Shandong Corporation of China Aluminum Co., Ltd., Zibo 255065, China） Abstract: Low aluminum, low-silicon ore dissolution of high-iron red mud, Laboratory of Experimental study of magnetic roasting carbothermal reduction, by means of SEM-EDS, XRD, DTA-TG, IR method to control the technical conditions, magnetic roasting and magnetic separation bonanzairon concentrate and tailings test magnetic susceptibility achieve a 90% recovery in 75% total iron grade of iron concentrate at 65%. While taking advantage of the high-iron red mud magnetic separation of iron concentrates the Slon series of high gradient the pulse magnetic separation machine research, analysis of data and magnetic separation of cutting-edge technology, and high-iron red mud extracted iron concentrate project economy than right, is expected to realize the the fully comprehensive utilization of red mud to achieve zero emissions of the industrial waste residue of alumina. Key words: Metallurgical Technology；High-iron red mud；Divalent metal 2高铁赤泥磁化焙烧提取铁精粉试验 2.1原理 高铁赤泥中主要的矿物组成为方解石、石英、钠硅渣、赤铁矿、针铁矿和伊利石等。赤泥中的氧化铁含量为30%左右，以赤铁矿、针铁矿为主要存在状态，二者的含量占赤泥总铁含量的95%以上，其次为硅酸铁盐类[1]。磁化焙烧是加热到一定温度后在相应气氛中进行物理化学反应，还原焙烧适用于赤铁矿和铁矿，常用的还原剂有，和等，铁矿在加热过程中首先排出化合水，变成不含水的赤铁矿，然后按反应被还原成磁铁矿赤泥中铁元素的存在形态大致有Fe2O3 ，Fe3O4，FeOOH，NaFeO2，FeS2，FeO及其与2FeO·SiO2 和FeO·Al2O3等的复合化合物。它们的还原顺序于分解顺序相同： 3Fe2O3 2Fe3O4 6FeOOH 6FeO 6Fe。 拜耳法赤泥的主要化学成分（%） SiO2 Fe2O3 Al2O3 CaO MgO TiO2 Na2O K2O 15.16 47.23 19.25 2.72 0.58 2.67 9.38 0.53 图1　铝土矿和高铁赤泥中铁矿物的XRD和DTA图谱 A-针铁矿;B-赤铁矿;C-钛铁矿;D-磁铁矿;E-赤泥中钛铁矿;H-赤铁矿;GO-针铁矿 2.3实验过程与条件 按照处理低品位铁矿石的办法，对原生赤泥直接配碳进行低温还原焙烧，然后对焙烧渣脱碳处理后，进行球磨，磨细后的焙烧渣再进行磁选，得到铁精粉和尾矿渣。 主要实验条件：温度：600度；时间：1小时；干基配碳比：15%。 2.4技术控制要点 保持还原气氛，控制原生赤泥还原焙烧的磁化率。 脱碳处理过程中防止还原物的二次氧化与磁性铁的二次包覆，控制铁精粉的杂质含量，即铁精粉的二次除杂。磁选过程控制铁精粉的品位，保持高的回收率。 3试验结果与分析 实验室得到铁精粉3000g。实验结果磁化焙烧-分离分选数据如下表2.，全部按照Fe2O3折合计算