The problems of the first law 1.1 a lead bullet is fired at a frigid surface. At what speed must it travel to melt on impact, if its initial temperature is 25℃ and heating of the rigid surface of the rigid surface is neglected? The melting point of lead is 327℃. The molar heat of fusion of the lead is 4.8kJ/mol. The molar heat capacity CP of lead may be taken as 29.3J/(mol K) Solution: 1.2 what is the average power production in watts of a person who burns 2500 kcal of food in a day? Estimate the average additional powder production of 75Kg man who is climbing a mountain at the rate of 20 m/min Solution 1.3 One cubic decimeter (1 dm3) of water is broken into droplets having a diameter of one micrometer (1 um) at 20℃. what is the total area of the droplets? Calculate the minimum work required to produce the droplets. Assume that the droplets are rest (have zero velocity) Water have a surface tension of 72.75 dyn/cm at 20℃ (NOTES: the term surface energy (ene/cm2) is also used for surface tension dyn/cm) Solution 1.4 Gaseous helium is to be used to quench a hot piece of metal. The helium is in storage in an insulated tank with a volume of 50 L and a temperature of 25℃, the pressure is 10 atm. Assume that helium is an ideal gas. when the valve is opened and the gas escapes into the quench chamber (pressure=1 atm), what will be the temperature of the first gas to hit the specimen? As the helium flows, the pressure in the tank drops. What will be the temperature of the helium entering the quench chamber when the pressure in the tank has fallen to 1 atm? Solution: 1.5 An evacuated (P=0), insulted tank is surrounded by a very large volume (assume infinite volume) of an ideal gas at a temperature T0. The valve on the tank is oeened and the surrounding gas is allowed to flow suickly into t(e tank until the pressure insi`e the tank is equals the pressure outside. Assume that no heat flow takes place. What is the0final tempeture kf tèe gaS in the tank? The heat cap!cit