(不锈钢热处理CEC-JW.C-015Gbac5619.docVIP

CEC维表21-1 成 飞 集 团 电 子 公 司 CAC GROUP ELECTRONICS TECHNOLOGY Co., Ltd. 沉淀硬化不锈钢的热处理 工 艺 规 程 HEAT TREATMENT OF PRECIPITATION HARDEDING STEEL 编号 ITEM 版次 ED 第1页 共15页 CEC-JW.C-015 A PAGE 1 OF 15 车间shop: 依据according to: BAC5619（H） 说 明 1、本规范规定了波音17-7PH、17-4PH和15-5PH钢沉淀硬化热处理要求。Description: This specification establishes the requirements for the heat treatment of precipitation hardening steels 17-7PH、17-4PH and15-5PH for boeing. 2、炉子和冰箱应安装仪表并按BAC5621定期校验精度和测量均匀性。 Furnaces and refrigeration equipment shall be instrumented and periodically tested for accuracy and uniformity in accordance with BAC5621. 3、装卸设备能使零件顺利入炉和转移，其不能影响加热或炉子的加热控制性能，若有必要，加热期间可使用夹具。 Provide handing equipment for inserting the steel into the furnace and removing handing equipment shall not interfere in any way with the heating or heat controlling characteristics of the furnaces. When necessary, use suitable fixtures for support during heating. 4、装卸设备表面应清洁，无影响零件和炉内气氛的杂质。 Surface of handing equipment shall be kept clean and free of foreign materials that could contaminate parts or the furnace atmosphere. 编 制 校 对 质 保 审 核 批 准 CEC维表21-2 成 飞 集 团 电 子 公 司 CAC GROUP ELECTRONICS TECHNOLOGY Co., Ltd. 沉淀硬化不锈钢的热处理 工 艺 规 程 HEAT TREATMENT OF PRECIPITATION HARDEDING STEEL 编号 ITEM 版次 ED 第2页共15页 CEC-JW.C-015 A PAGE 2 OF 15 车间shop: 依据according to: BAC5619（H） 序号 S/N 工 序 OPERATION 设 备 EQUIPMENT 操 作 说 明 OPERATION DESCRIPTION 备 注 REMARK 成份COMPOSITION 温度TEMP 时间TIME 其 它 要 求 OTHER REQUIREMENT 1 制造控制 Manufacturing control （1） Temperature tolerances and controls 所给的温度范围为1000~1100°F（538~593℃），而炉子容差为±25°F（±14℃），则控制设定在 1025~1075°F（552~579℃）之间），如果工艺温度范围等于炉子容差，控制设定在工艺范围的中点。 All indicated or recorded temperature shall be within the specified temperature range， set furnace controls at a temperature which ensure that all points within the working zone of the furnace are within the specified temperature range. （e.g