材料成型金属学ch07-1金属在塑性加工中组织与性能变化的基本规律摘要.pptVIP

7.1 金属在塑性加工中组织与性能变化的规律Change of structure and property in cold forming 7.1.1 金属在冷塑性加工中组织与性能的变化 多晶金属冷变形→等轴晶粒沿主变形方向拉长 大变形量→晶粒呈纤维状→称纤维组织 1. fiber structure 纤维组织 If we observe the sample after deformation, we can find that original equiaxial grains are elongated along the principle deformation direction. When the deformation is very large, the grains cannot be distinguished clearly. It looks like fiber, so it is called fiber tissue. ε↑→dsub ↓→σ↑ subgrain strengthening 亚晶强化 变形达到一定程度,变化减小。 3. deformation texture 变形织构 杂乱排列的晶粒,通过变形,各晶粒取向大体趋于一致,为“择优取向” （preferred orientation distribution）。 具有择优取的组织称为 “变形织构” （deformation texture )。 板织构 plate texture 轧制rolling 或者宽展很小的矩形件镦粗 upsetting 平面变形plane strain 某一晶向//轧向 某一晶面//轧面 Preferred Orientation Also called crystallographic anisotropy Slip planes tend to align themselves with the direction of deformation method for measuring texture: x-ray diffraction x射线衍射 pole figures极图 random distribution of orientation 　无择优取向 cube texture立方织构 7.1.2. 力学性能的变化change of mechanical properties 一. 加工硬化 work hardening 金属在变形过程中随着变形程度的增加,强度和硬度明显增加,塑性迅速下降的现象称为～ 单晶体 single crystal 加工硬化曲线 曲线斜率θ=dτ/d?,加工硬化率hardening ratio 剪切力ττc 弹性阶段, ττc 塑性变形阶段 塑性变形阶段的曲线可分为三阶段： 易滑移阶段 线性硬化阶段 抛物线硬化阶段 Ⅱ.线性硬化阶段—多系滑移multiple slip system 多系滑移→位错反应→位错塞积缠结→胞状亚结构 必须加大外加切应力→变形抗力↑→硬化率↑ Ⅲ.抛物线硬化阶段—交滑移cross slip 交滑移→异号位错抵消→位错密度↓→硬化率↓ Influencing factors: (1)晶体结构 h.c.p(如镁)一组滑移面 →单系滑移→硬化率↓ →易滑移阶段↑ b.c.c. f.c.c滑移系较多 →硬化率↑ 二.各向异性anisotropy 加工方式不同→不同织构 →不同方向上 性能的差异 正面影响 positive effect 磁性材料magnetic material 例:变压器用硅钢片 (110) [001] 高斯取向 〈100〉易磁化方向 沿轧制方向磁导率↑ 铁损↓ 7.1.4. Changes of other mechanical properties 一.Density金属密度 crack 裂纹cavity 空洞→density↓ 二. Electric conductivity 导电性 Gene