常温固化耐磨防腐涂料的研制 夏博文 （陕西科技大学造纸工程学院 陕西 西安710021）摘要：本文研究的是以聚氨酯为基体，添加聚四氟乙烯、氧化铁、钛白粉等填料、研制出一种双组分常温固化涂料。通过L9 (43)正交试验和极差分析得出最佳配方。当聚氨脂的用量为10g、聚四氟乙烯为4g、钛白粉为0.g、氧化铁为0.g时，测试结果表明涂层综合性能最佳：涂层的附着力为0级，硬度为3H，耐磨性为用漆膜磨耗仪JM-Ⅳ 转2500圈时磨耗量为0.018g。 关键词：聚氨酯；常温固化；耐磨防腐涂料 THE REARCH OF WEAR RESISTANT ANTICORROSIVE COATING ON SOLIDITICATION UNDER ROOM TEMPERATURE ABSTRACT：In this article, the wear resistance and anticorrosive coat, which used Polyurethane as carrier and TiO2, Fe2O3 as filling and turn to solid in room temperature was discussed. Through the even design and orthogonal experiment, the best direction for producing coat was chose by the orthogonal experiment, and the further study for the ability of the coating. The results showed: comprehensive properties of the coating film were the best. Under the 2500 circle force, the abrasion quantum were 0.018g, the hardness of the coating was 3H,and the adhesion rank was 0. 1前言 我国聚氨酯涂料的研制和开发始于20世纪50年代，从80年代以来尤其是近20年得到突飞猛进的发展。聚氨酯涂料在产品产量上跃居涂料行业的第三位，仅次于醇酸树脂漆和酚醛树脂漆。聚氨酯之所以能异军突起，是因为它具有许多独特的性能被广泛的应用于汽车、火车、飞机、船舶、自行车、摩托车、机床、电子仪表、电器、建筑、桥梁、木器家具以及居室装饰等领域和工业部门的装饰和保护，同时也适用于石油设施、化工设备、管道、海上平台、海港设施、重型机械等的防腐和装饰。到目前为止，还没有哪种聚合物能像聚氨酯那样可在塑料、橡胶合成纤维涂料黏合剂及灌浆材料等各个方面都可以取得如此广泛的应用[1]- [2]。 本课题研究的是常温固化耐磨防腐聚氨酯涂料的研制。它不仅具有一般聚氨酯所具有的优异的柔韧性、耐冲击性、耐化学药品性、高光泽保护性、耐低温，还能适用于对耐磨要求较高的场所。由于它能够在常温下固化，所以施工方便，适用范围非常广泛。 2试验材料与工艺路线 1、试样： A3钢：50mm×50mm×5mm 2、主要仪器：天平、烧杯、玻璃棒、水浴锅、搅拌器、电源、胶头滴管、铅笔、量筒、毛刷、CM-无釉砖耐磨实验机。 3、实验原料 表1 原料及其规格 原料 规格 TDI 分析纯 蓖麻油 化学纯 丙酮 分析纯 二甲苯 分析纯 醋酸丁酯 分析纯 三乙醇胺 分析纯 二月桂酸二丁基锡 分析纯 201硅油 分析纯 聚四氟乙烯 800目 石墨 600目 二硫化钼 600目 三氧化二铬 600目 二氧化硅 600目 青铜粉 600目 氧化钛 600目 4、工艺路线： 试样的表面处理 → 聚氨酯的配制 → 配制涂料 → 刷涂料 →性能测试 （1）试样预处理的目的及方法： 除去金属表面附着的异物，使金属表面具有一定的耐蚀性、提高底金属与涂膜的附着力。预处理的方法：机械预处理和化学预处理。 （2）聚氨酯的制备： 本实验采用的是一次加料法，即把配料一次性加入反应釜中，然后升温反应，以制得最终的预聚物。一次加料法生产工艺简单、稳定、省去滴加装置，而且，产品色泽较浅。具体工艺如下：将TDI按所定初值滴加入蓖麻油中，然后加入丙酮，由于聚氨酯的固含量为50%，加入丙酮的量为TDI与蓖麻油总量的和。将溶液混合好后，用搅拌器持续搅拌，并在水温浴中加热，恒温40～50℃反应三小时[3]。 （3）涂料添加物的确定： 由均匀设计可得出：（聚氨酯的用量为10g） 三乙醇胺和二月桂酸二丁基锡的量均为0.0125g； 聚四氟乙烯的用量不超过2%，钛白粉和氧化铁的用量不超过15%；