(水玻璃复合材料.docVIP

水玻璃复合材料 摘要：水玻璃复合材料是一种利废、节能、低污染的高绿色度材料，在国家提倡“节能减排”的形势下，研究和应用水玻璃环境友好型材料必然会引起良好地市场效益。本文对近年来国内外水玻璃的特性、改性、硬化机理和应用领域以及制备方法做了相应的研究。 关键词：水玻璃,复合材料,节能,溶胶-凝胶法 Sodium silicate composite materials Chen huan (mianyang vocational technical college material engineering analysis of 111 class Mianyang 621010) Abstract the sodium silicate composite materials is a recycling, energy saving, low pollution and high degree of green material, in the state advocates energy conservation and emission reduction in the situation, research and application of sodium silicate environment friendly materials will inevitably lead to good market benefit. In this paper the characteristics of sodium silicate at home and abroad in recent years, modification, hardening mechanism and application areas and preparation methods did corresponding research. Keywords sodium silicate, composite material, energy saving, sol-gel method  水玻璃是碱激发工业废渣胶凝材料中的一种重要原料，而碱激发工业废渣胶凝材料被认为是一种具有极大开发价值和应用前景的环境友好型胶凝材[1]-[2]。随着我国工业现代化进程的加速变化，各种工业大量产生钢渣、矿渣以及粉煤灰、冶金工业等主要工业产生的废渣对环境的影响是及其严重的，因此对工业废渣废弃资源再资源化来取代水泥的研究无凝显得重要。水玻璃材料的研发将是一个全新的方向，预期成为一种节能、低成体、环境友好性好的高性能材料，为实现我国材料行业的可持续发展奠定基础。 一 水玻璃的简介 水玻璃是多种聚硅酸的复杂溶液，是一种性能良好的涂料。主要成份为氧化钠、二氧化硅和水。 水玻璃可分为硅酸钠水玻璃、硅酸钾水玻璃、硅酸锂水玻璃、硅酸盐季铵水玻璃和钾钠硅酸盐水玻璃等。 二 水玻璃的特性 2.1 黏结力和强度较高 水玻璃硬化后的主要成份是硅凝胶固体，比先前的表面积大，因而具有较高的黏结力。但是水玻璃自身质量，配合料性能及施工养护对强度有显著影响。 2.2 耐酸性好 可以抵抗除氢氟酸（HF)、热磷酸和高级脂肪酸以外的所有有机酸和无机酸。 2.3 耐热性好 硬化后形成的二氧化硅网状骨架，在高温强度下下降很少，当采用耐热、耐火集料配制水玻璃砂浆和混凝土时，耐热度可达1000℃，因此水玻璃混凝土的耐热度也可以理解为主要取决于集料的耐热度。 2.4 耐碱性和耐水性差 因混合后易均溶于碱，故水玻璃不能在碱性环境中使用。同样由于氟化钠、碳酸钠均溶于水而不耐水，但可采用中等浓度的酸对已硬化的水玻璃进行酸洗处理来提高耐水性。 三 水玻璃的改性 3.1 水玻璃的物理改性 钠水玻璃的老化过程是其内部能量缓慢释放的过程，那么消除水玻璃的老化就必须向老化的水玻璃体系中输入能量，输入能量的方法很多：主要有超声振荡、磁场处理。 3.1.1 超声振荡处理 1.将装有钠水玻璃的容器置于超声波清洗器的洗槽内，槽内放有40mm深的水，超声频率13.5—18.0HZ。开动超声波清洗器，振动一段时间，对水玻璃进行改性，香水玻璃补充能量，以提高其抗老化性能，这种方法用于实验室研究，能耗低，设备简单。 2．将超声发生器的致磁伸缩杆直接插入盛有水玻璃的容器中，超声频率为16.0—25.0HZ，功率视水玻璃粘借结剂的处理量而定，主要应用与实际生产中。 3.1.2磁场处理 磁场处理最常适用于中模水玻璃，水玻璃粘结剂磁化后应该尽快使用，放置一段时间后会有强度衰退的现象。 3.2 水玻璃的化学改性 水玻璃的化学改性是往水玻璃中添加一种或数种其他物质以阻缓水玻璃的老化，减少因