减振器前叉管断裂原因分析.docVIP

减振器前叉管断裂原因分析 张全新 （重庆钢铁研究所有限公司，重庆 400084） 摘 要：本文通过对摩托车减振器前叉管的化学成分、硬度、断口形貌及金相组织进行检验和观察，分析和讨论了前叉管的断裂性质及原因，从而得知该摩托车减振器前叉管的断裂是材料中存在严重的非金属夹杂物所导致的疲劳断裂。 关键词：前叉管；非金属夹杂；疲劳断裂 Fracture Analysis of the Shock Absorber Front Fork Tube ZHANG Quan-xin （Chongqing Iron and Steel Research Institute Co.Ltd., Chongqing 400084,China） Abstract：the cause and the crack nature of the front fork tube by means of the tests of motorcycle front fork tube shock absorber of the chemical composition, fracture morphology, hardness and metallurgical structure. Then it came to know that the crack was caused by the fatigue fr