蜂窝式SCR脱硝催化剂制造中的技术问题 李守信1，2 于光喜2 颜少云2 陈青松3 210042 3.陈青松 青岛腾禹环保有限公司 266101 [] 本文从催化剂的组成出发，介绍了V-W-Ti型催化剂的主要成分及作用，结合生产实践讲述了V-W-Ti型蜂窝式SCR脱硝催化剂制造的工艺过程，指出了影响催化剂产品质量的关键工序，并对它们进行了理论分析。 [关 键 词] SCR脱硝催化剂；混炼；一段干燥；热力干燥；焙烧 Technical Problems in Manufacturing of Cellular SCR DeNOx Catalyst LI Shouxin1，2YU Guangxi2,YAN Shaoyun2,CHEN Qingsong3,HUA Panlong2,HUA Jing2 1, Environmental Science and Engineering College of North China Electric Power University,Baoding,Hebei 071003,China; 2, Jiangsu Wande Catalyst Science and Technology CO., Ltd.,Yangzhou,Jiangsu. 210042; 3, CHEN Qingsong, Qingdao Tengyu Environmental Engineering Co., Ltd. 266101,China Abstract Starting from the composition of catalyst, this article introduced the main ingredients and functions, combining with production practice about V-W-Ti cellular SCR DeNOx catalyst manufacturing process, points out the influence of catalyst quality key procedure, and has carried on the theoretical analysis. Key words SCR DeNOx catalyst；mixing；the first drying；thermal drying； calcination 面对氮氧化物污染的加剧，各种控制污染的技术相继出现，应用在燃煤电站锅炉上的成熟烟气脱硝技术主要有选择性催化还原（ Selective Catalytic Reduction，简称SCR）、选择性非催化还原 (Selective Non-Catalytic Reduction，简称SNCR)以及SNCR/SCR 混合烟气脱硝技术。[1]。 由于选择性催化还原法（SCR）具有脱硝效率高（可达85%以上），能够满足严格的排放要求，因此，SCR技术在世界市场的占有接近70%，而在我国，据统计，这个数字已突破95%。 催化剂是SCR法的主体，它的质量和性能直接决定着脱硝效率的优劣。因此，世界各国的研究人员都把SCR催化剂的研发作为重点。目前实现大规模应用的是V-W-Ti型的蜂窝式催化剂，它的应用占到70%以上的市场份额。 本文结合生产实践，谈谈SCR脱硝催化剂制造中的几个技术问题。 工业固体催化剂通常是由部分组成的[]： 1.1 活性组分 能单独对化学反应起催化作用的物质，有时可以单独使用。助催化剂 这类物质并没有催化活性，然而它的少量加入，却能明显活性组分的催化性能，同时可以提高活性组分的选择性或稳定性。 载体 的作用提供大的比表面积，提高活性组分和助催化剂的分散度。其次是改善催化剂的传热、抗热冲击和抗机械冲击的性能。 除了上述成分之外，在工业催化剂中有时还要加入些组分，如粘合剂、造孔剂等。 V-W-Ti型催化剂中主要成分及作用 2.1 V2O5：活性组分，主要作用是催化NOx向N2还原的反应速度。但同时也可以催化SO2→SO3的转化，因此，需要严格控制含量，含量过高不仅会增大SO2的转化率，而且还会因结晶减少其比表面积，从而降低脱硝效率。 WO3：助催化剂，主要作用是提高V2O5的活性和选择性。在一定程度上还可阻止SO2的氧化，同时可以增催化剂的反应温度范围，改善催化剂机械结构和晶体性质，提高催化剂的抗磨性。 当燃煤中砷含量较高时，通常用MoO3替代WO3催化剂的砷中毒。，加MoO3的催化剂活性低于加WO3的催化剂。同时MoO3还使少量的NOX转化成N2O N2O是温室气体，对大气环境危害很大，所以如果燃煤中含砷较低，尽可能地不用MoO3。