加食盐焙烧的石灰铁水脱硫实验研究.docVIP

加食盐焙烧的石灰铁水脱硫实验研究 夏幸明　　　　　　朱英雄 (宝山钢铁(集团)公司)　　(东北大学) 摘　要　石灰的物性是影响其铁水脱硫能力的主要因素之一。在实验室条件下，通过对加食盐焙烧的石灰铁水脱硫试验研究，表明石灰的活性度并不完全对应其铁水脱硫能力；加食盐焙烧的石灰气孔率高、气孔尺寸大、气孔贯通率高，具有较高的铁水脱硫能力。关键词　加食盐焙烧的石灰　物理性质　铁水脱硫 EXPERIMENTAL STUDY ON HOT METAL DESULPHURIZATIONWITH LIME CALCINED WITH SALT XIA Xingming (Baoshan Iron and Steel Corp.) ZHU Yingxiong (Northeastern University) ABSTRACT　The physical properties of the lime are one of the important factors influencing efficiency of the lime in hot metal desulphurization.The hot metal desulphurization with the lime calcined with salt has been investigated in laboratory.It is shown that the lime activity is not directly correlated to desulphurization efficiency.The lime calcined with salt has high porosity,large pore size and high penetration rate of pores,and therefore has higher desulphurization ability for hot metal.KEY WORDS　lime calcined with salt,physical properties,hot metal desulphurization 1　前言 　　用石灰作为铁水的脱硫剂，一直为人们所关注。为了改善石灰的脱硫效果，人们采取了诸如使用活性石灰、添加其它助脱硫剂以及改善动力学条件等方面的措施。其中在活性石灰的使用和研究中，人们较多注重于石灰的高活性度。然而通常的活性石灰虽然气孔率较高、比表面积大，但气孔的平均尺寸较小。在炼钢的条件下，石灰的活性度与其实际的反应能力较为相符。但作为铁水的脱硫剂，由于CaO的脱硫过程为一固—液相反应，而且一般处理过程中粉剂在铁水中停留的时间又很短，因此石灰的脱硫效率在很大程度上取决于反应初期CaO与铁水的接触状况。石灰中的孔隙尺寸越小，铁水向其内部的渗透越困难，也就不能最大限度地发挥其应有的脱硫能力。研究表明，在铁水条件下，要使铁液能渗入到石灰孔隙内，其石灰的平均孔径必须大于2 μm。　　加食盐焙烧石灰是近年来国内外为提高竖窑焙烧石灰质量的一种有效措施。采用这种技术焙烧的石灰不仅气孔率高，而且气孔尺寸大，气孔贯通率也高，石灰的反应能力尤其是初期反应能力强，已在炼钢生产中发挥了显著的作用。但这种石灰是否在铁水脱硫中也具有良好的作用，目前尚缺少一定的研究和实践。为此，本文在研究了加食盐焙烧的石灰特性基础上，进行了这方面的工作。 2　实验条件 2.1　实验原料　　铁水脱硫所用脱硫剂为如表1所示条件下不加食盐与加食盐焙烧的两类12种石灰。 表 1　脱硫用石灰活性度　mLTable 1　The lime activity for desulphurization　　mL 焙烧温度/℃ 恒温时间/min 30 90 180 900 — 272/364 — 1　000 — 425/438 — 1　100 345/438 162/440 59/438 1　200 — 59/406 — 　　注：不加食盐焙烧的石灰活性度/加食盐焙烧的石灰活性度。　　实验所用生铁成分如表2所示。 表 2　实验用生铁成分　　%Table 2　The chemical composition of iron for experiment　　% C Si Mn P S 4.31 0.54 0.090 0.089 0.046 2.2　实验设备　　图1为实验所用的装置简图。 图 1　实验装置示意图Fig.1　The schematic diagram of experimental apparatus 1—自动温度控制仪；2—硅碳棒发热体；3—炉管；4—炉体； 5—刚玉坩埚；6—热电偶；7—耐火砖 2