氯化橡胶云铁防锈漆.docVIP

氯化橡胶云铁防锈漆 Intended Uses 用途 适用于船舶、煤气罐、海港码头、海上钢结构飞溅区、石油化工设备外壁，管架及其他钢结构防蚀、也可涂在混凝土物件作为保护层，由于云母氧化铁为鳞片状颜料，具有独特的屏蔽性能，颜料能定向平行重叠排列，形似“鱼鳞”一般的搭接结构，因此涂膜具有优良的防锈、防潮、耐化学腐蚀性能。 Suited for anticossive protection of vessel, gas tank dock, spatter part of marine steel structure, exterior petroleum and chemical equipment. Also can be painted on cement structures for protection. Due to micaceous iron oxide, a scale-like pigment which may overlap and arrange parallel and form an orientation in similitude of fish scale after film formation, it is possessed of excellent property of anti-corrosive and resistance to chemicals. Product Description 产品简介 灰黑色，底漆或中涂漆 Grey black, primer or intermediate coating? Product Information 产品数据 Volume Solids 固体份 ≥40% Dry Film Thickness干膜厚度 70microns equivalent to 175 micrions of wet film??????????? 70微米相当于175微米湿膜厚 Theoretical Coverage 理论涂布率 4.1 m2 /Kg???? ??????????4.1平方米/公斤 Practical? Coverage 实际涂布率 Allow appropriate loss???? 允许适量损耗 Application Details ? 施工详述 ? Mix Radio 混合比 One pack ???????????单罐装 Method of Application???? 施工方法 ? ?? Airless Spray????????? 无空气喷涂????????? Recommended??????? 推荐采用 ? ?? Brush or Roller??????? 涂刷或辊涂????????? Recommended??????? 推荐采用 ?? ?? Conventional Spray???? 传统喷涂??????????? Not Recommended??? 不推荐使用 ?? Thinner????????????????????? 稀释剂?????????????? ???C001 Cleaner????????????????????? 油漆设备清洗剂????????? C001 Pot Life??? ?????????????????使用期????????????????? Not limit????????????? 不限制 Storage????????????????????? 贮存期????????????????? One year?????????????? 一年 Drying time 干燥时间 ? Substrate Temperature 底材温度 Touch Dry 表干 （H） Hard Dry 硬干 (H） Over coating Interval 覆涂间隔 ? Mix最短 Max最长 ? 25℃ 0.5 8 0℃ 24 hour 小时 24 8 hour 小时 30 6 hour 小时 ? Not limit 不限 ? Storage and Handling 贮存与管理 ?Storage?????? 贮存?????????? Store in cool and dry conditions?? 贮存于阴凉干燥处 Pack size???? 包装规格????? 25Kg in 20 liter container???? ?????25公斤装于20公升容器中 Flash Point??? 闪点????????? ≥31??????????????????????? ?????高于23 Specific