高岭土和矿粉对混凝土强度的影响.docVIP

高岭土和矿粉对混凝土强度的影响 董晶亮 摘要：通过胶砂试验的方法研究了高岭土﹑矿粉两种矿物掺合料对水泥胶砂的影响。由试验结果得知， 28 天龄期时, 随高岭土量的增加, 水泥胶砂抗压强度和抗折强度均下降;然而高岭土的细度和煅烧与否胶砂的强度没有影响。 随矿粉掺量的增加, 胶砂28天抗压强度增加，抗折强度也会增加。 关键词：胶砂，高岭土；矿粉；细度；煅烧；抗折强度；抗压强度 The influence of ground slag and china clay to the strength of concrete Abstract: Some experiments were done in order to study the influence of ground slag and china clay to the strength of cement mortar. In 28 ages, with the quantity of china clay increased, the rupture strength and compressive strength of cement mortar decreases but the fineness and calcined of china clay have no influence to the strength of cement mortar, with the quantity of ground slag increase, the compressive strength of cement mortar is enhanced, and the rupture strength of cement mortar is also enhaned. Key words:cement mortar ;china clay ;ground slag;fineness;calcined Compressive strength;rupture strength 前言 混凝土是当前用量最大的建筑材料，据不完全统计世界水泥产量已超过15亿吨，折算成混凝土应不少于45亿立方米，由于水泥生产消耗大量的能源和资源，并且产生大量的污染物，给经济和环境带来了沉重的负担。因此世界各国都在满足工程需要的前提下，尽量的减少水泥用量。目前用的最多的是在混凝土中掺入活性矿物掺合料来取代水泥，改善混凝土的性能达到减少水泥用量的目的。本文主要是研究高岭土的不同细度，煅烧与否及在不同水胶比下混凝土的抗压和抗折强度，和矿粉在不同水胶比下胶砂的抗压强度和抗折强度。高岭土有很强的结合性和耐酸性能，掺入混凝土中能够提高混凝土的密实性，抗渗性，和耐酸腐蚀性。同时高岭土有很好的可塑性，能够改善混凝土的塑性。矿粉具有自身弱水硬性和火山灰活性的作用，在水泥水化产物CH和石膏的激发下具有较高的活性，矿粉吸收部分CH发生二次水化反应生成CSH凝胶，从而改善了界面区CH的取向度，减少了CH晶体的尺寸，有利于混凝土力学性能的提高和耐久性的改善，现在矿粉代替水泥量达到40%以上。本文之所以选择高岭土和矿粉是因为两者的活性相差很大，同时高岭土有很多优秀的物理化学性质，利用它对混凝土进行改性也是一个很不错的选择。本文以胶砂实验为基础，确定了掺和料活性对混凝土强度的影响。 实验设计 本文采用胶砂试验进行研究。 2.1 原材料 水泥: 大连小野田42.5R普通硅酸盐水泥 细集料: 采用标准砂 水：自来水 高岭土： 矿粉： 2.2 实验方法 本试验重点测试0.46,0.42,0.38,0.34水胶比下矿粉和高岭土等量取代水泥，10%-40%变化对混凝土强度的影响规律，掺合料采用煅烧1250目，非煅烧235目，非煅烧1250目，非煅烧的4000目四种类型的高岭土和矿粉共五种。矿粉的型号是 以水泥胶砂试验为基础，成型胶砂试件，在标准养护条件下养护28天，测得其28天的抗折强度和抗压强度，通过分析得出了高岭土，矿粉对混凝土强度影响的关系，并提出几点假设。 2.3 实验结果 掺入掺合料水泥胶砂28天的抗折和抗压强度(MPa) 煅烧1250目高岭土 非煅烧325目高岭土 非煅烧4000目高岭土 非煅烧1250目高岭土 矿粉 水胶比 水泥取代量 抗折强度 抗压强度 抗折强度 抗压强度 抗折强度 抗压强度 抗折强度 抗压强度 抗折强度 抗压强度 0.46 0% 10.7 63.3 10.7 63.3 10.7 63.3 10.7 63.3 10.7 63.3 10% .7 56.6 10.5 57.4 10.1 57.4 10.0 57.3 9.83 62.0 20% 8.73 49.7