超高强微钢纤维增韧混凝土制备和其力学性能的研究(修改).docVIP

超高强微钢纤维增韧混凝土的制备 及其力学性能研究 王冲1, Liza O’Moore2 1: 重庆大学材料科学与工程学院，重庆，400045 2: Department of Civil Engineering, the University of Queensland, QLD 4072, Australia 摘要：高脆性是超高强混凝土难以被广泛应用的主要原因之一。为降低脆性，本研究利用长度为6mm与13mm的三种微钢纤维，制备了超高强微钢纤维混凝土，研究了不同纤维长径比及掺量条件下混凝土的力学性能指标，其中包括ASTM C-1018方法测试超高强微纤维混凝土的抗弯韧性。结果：的初始裂缝强度、抗折强度和韧性指数初始裂缝强度、抗折强度和韧性指数长度为6mm的纤维抗压强度掺量强度混凝土劈拉强度弹性模量有所增加。关键词：微钢纤维；超高强混凝土；制备；力学性能 中图分类号：TU528.572 文献标识码：A Research on Preparation and Mechanical Properties of Super-high Strength Steel Micro-fiber Toughened ConcreteWang Chong 1, Liza O’Moore2 1: College of Materials Science and Technology, Chongqing University, Chongqing 400045, China 2: Department of Civil Engineering, the University of Queensland, QLD 4072, Australia Abstract: Super high strength concrete (SHSC) is difficult to be applied in civil engineering widely because of its high brittleness. The objective of this research is to reduce the brittleness of super high strength concrete by adding steel micro-fibers of 6 mm and 13 mm length. Mechanical properties of concrete were investigated under condition of different aspect ratio and different volume, which including flexural toughness measured by ASTM C1018. The test results show that energy absorption capability of SHSC were enhanced with increase of fiber volume. Compared with control mix, the effectivest improvement of the first crack strength, flexural strength and toughness indexies were investigated in the case of 1.0% fiber volume, which were closed to that of 2.0% fiber volume. A biger compressive strength of SHSC was tested in the case of 2.0% volume when 6 mm length fiber added, but higher compressive value were measured under the condition of 1.0% when 13 mm fibers added. The results also show that tensile strength and Young’s modulus of SHSC were improved by adding steel micro-fiber. It is concluded in this research that a reasonable fiber volume should be applied when steel micro-fiber are used to improve the toughness of S