AP1000一体化堆顶三脚架组件磁粉检测设备与工艺研究--发表在电站辅机上综述.doc

AP1000一体化堆顶三脚架组件磁粉检测设备与工艺研究 朱跃德1 李守彬12 马占云1 1山东核电设备制造有限公司 山东 海阳 265118 2 哈尔滨工业大学（威海）山东威海 264200 摘要：通过分析AP1000一体化堆顶三脚架组件的制造过程和检测要求，研究了在执行产品磁粉检测过程中需要考虑的结构特点和技术要素，依据研究分析结果计算确定了检测设备参数和工艺方案，通过厂家配合完成设备制造、调试并投入了使用，为AP1000设备制造工作的顺利开展提供了必要条件。 关键词：三脚架组件；磁粉检测；设备参数；工艺参数 Researches for the magnetic testing equipment and technology of AP1000 IHP lift RIG TRIPOD Zhu yue-de1 Li shou-bin12 Ma zhan-yun1 1.Shandong Power Equipment Manufacture Co., Ltd，Haiyang Shandong, 265118 China) 2.Harbing Institute of Technology WeiHai, 164200 China Abstract: This article analysis the manufacture process and the testing requirements of AP1000 IHP lift RIG TRIPOD, Have a research for the magnetic testing process which based on the technology basics and construction .Based on the results we make the project for the equipment preferences and technology preferences and then make it installed or used successfully, All of above make the conditions for the manufacture of the AP1000 products. Key words: lift RIG TRIPOD, magnetic testing, equipment preferences, technology preferences 1 引言 三角架组件（如图1所示）作为一体化堆顶吊装系统提升装置的关键核级安全相关物项是核反应堆堆芯换料的核心部件，它主要有支杆、U型夹、Y型块、超大型吊耳等复杂外形件组成，主要作用是在堆芯换料时将压力容器顶盖和一体化堆顶组件一同起吊。其中该组件中提升杆的测试拉力为230吨，三脚架的测试拉力为700余吨，连接器的测试拉力为800余吨，所以该组件制作安装要求极为严格，分别经过冶炼、锻造、热处理、机械加工、理化及无损检验、载荷试验等多个环节[1]。 图1 IHP三脚架组件 目前比较成熟的自动磁粉探伤设备主要针对外形简单的板状或轴形工件，而对于复杂外形的工件没有通用的自动检测设备，只能根据工艺要求进行针对性的设计．面对这一特殊的新产品，本文从产品结构特点、检测技术与验收要求对其中的磁粉检测设备参数、检测工艺等进行了专项分析研究，与设备生产厂家共同完成了该磁粉检测备的研制并顺利完成首台AP1000三脚架组件的检测工作。 二 检测工艺的制定 按照产品技术规格书APP-MV10-Z0-201的要求AP1000三脚架组件各零件的磁粉检测分别在最终机加完毕和载荷试验后按照ASTM A275或ASTM E709的技术要求双向对关键物项做100%MT检测。验收标准依据ASME锅炉及压力容器规范1998版，2000增补第三卷第一册NF分卷NF-5340进行，即： A．任何裂纹或线性显示拒收； B．任何尺寸大于5mm的圆形显示拒收； C．在一条直线上有4个或4个以上且边缘相距小于等于1.5mm的圆形显示拒收； D．在受评定的显示区域中最不利的位置上，任何一个表面积为4000mm2且该面积主要尺寸不超过150mm，这个面积内有10个或10个以上的圆形显示拒收。 考虑到复杂工件实施交流磁轭检测时发现缺陷的深度和近表面缺陷的灵敏度[2]不如直流磁粉检测，且基于产品使用特点、缺陷类别等因素，三脚架组件按ASTM A275标准作为检测技术要求：采用直流或全波/半波整流电方法进行检测。 2.1技术难点与重点： （1）三脚架各组件产品均属于外形复杂的特型件例如吊耳（如图2所示），包含平面、弧