硝酸预浸在阳极氧化膜封孔质量检测中的应用选编.doc

硝酸预浸在阳极氧化膜封孔质量检测中的应用 The Application of Prior Nitric Acid Treatment in the Assessment of Sealing Quality of Anodic Oxidation Coatings 硝酸预浸在阳极氧化膜封孔质量检测中的应用 [摘 要] 阳极氧化膜封孔质量的好坏，会直接影响阳极氧化膜的使用寿命。硝酸预浸是欧洲标准中规定的外部建筑用铝合金阳极氧化膜封孔质量检测的仲裁方法，文中考察了硝酸预浸在封孔质量检测中的作用，结果表明: 硝酸预浸有溶解氧化膜和扩孔的作用，在封孔质量检测中引入硝酸预浸，不仅严格了对封孔质量的要求，而且使得封孔质量的判别更为灵敏。 [关键词] 硝酸预浸; 封孔质量; 阳极氧化膜; 磷铬酸法 The Application of Prior Nitric Acid Treatment in the Assessment of Sealing Quality of Anodic Oxidation Coatings [Abstract] Sealing quality directly affects the service life of the anode anodic oxidation coatings. For the anodic oxida-tion coatings intended for exterior buildings，the phosphoric / chromic acid immersion with prior nitric acid treatment test method is specified as arbitration method in european standard. The effect of the prior nitric acid treatment on sealing quality test was studied. The results show that the prior nitric acid treatment has the action of dissolution and enlargement. The introduce of the prior nitric acid treatment in sealing quality test provides a more strict sealing quality test method，makes the sealing quality dis-crimination becoming more sensitive. [Key words] prior nitric acid treatment; sealing quality; alloy anodic oxide coatings; the phosphoric / chromic acid im-mersion method 前 言 铝阳极氧化膜属多孔结构，表面易因吸附灰尘、油脂等而发生污染，也易因受到腐蚀介质侵蚀而遭到破坏，因此必须经过封孔处理后才能投入使用。封孔质量的好坏直接影响到阳极氧化膜的使用寿命，是阳极氧化膜质量的重要指标之一。 封孔处理可以提高膜层的抗污染性、 电绝缘性和耐腐蚀性等 ，由此衍生出了许多评定封孔质量的方法，包括染色斑点法、导纳法 和酸浸法等。染色斑点法的特点是简单、快速，但结果的重复性和数据定量化比较差，目前多用于生产控制和在线快速检测。导纳法的特点是无损、快速，但其结果受阳极氧化膜厚度、着色方法、封孔工艺、陈化时间、存放环境等方面的影响。因此在我国使用很少。 酸浸法是通过阳极氧化膜酸浸前后的质量损失率来评定封孔质量，是目前应用最广泛的评定方法。它包括磷铬酸法和硝酸预浸磷铬酸法，在欧洲标准 EN12373. 1-2001 中规定，内部建筑和装饰用阳极氧化磷铬酸法，外部建筑用阳极氧化膜质量的检测采用硝酸预浸磷铬酸法。在国际标准化组织新修订的封孔质量评价标准中，也参照欧洲标准引入了硝酸预浸的磷铬酸法，并进行了类似的规定。但我国现行铝合金建筑型材标准GB5237.2-2008中并未对两种方法的差异和适用范围作出说明和划分。为此，文中对硝酸预浸在封孔质量检测中的作用进行了探讨。 硝酸预浸在阳极氧化膜封孔质量检测中的应用 一 试验前准备 1 仪器设备 表一 2 药品 3 试样的制备 选取同一型号（型号为ZWTYN-60，周长为）不同批次的8支阳极氧化型材，标记为1#～8#，型材均通过硫酸阳极氧化