煤和废塑料混熔燃烧动力学的研究.pdfVIP

煤和废塑料混熔燃烧动力学的研究 代祥社 （贵州大学就业指导中心 贵州贵阳 550003) 摘 要： 对不同比例的废塑料与煤粉混合，在不同混熔温度下制成样品进行燃烧动力学试验；结果表明：混熔样品的 F(a) －1/T 曲线的拟合直线相关系数绝对值均在 0.95 以上，表明实验的样品燃烧符合一级反应；混熔样品温度和塑料配比为 200 ℃、20～25%时的活化能最低，燃烧阻碍小。 关键词： 废塑料；煤；混熔样品；动力学 Study on Combustion Kinetics of the Blend Meltwith Coal and Plastic Waste DAI Xiang-she (The enter of employment coah of College of Materials and Metallurgy Engineering,Guizhou University, Guiyang, Guizhou 550003) Abstract:The combustion kinetics experiments are run by blending pulverized coal and plastic waste in different proportions and producing blend-melt samples in different combustion temperatures. The experiments show that all absolutevalues of correlation coefficients for fitting straight lines of SN curve F(a) －1/T of the blend-melt samples are above 0.95, which indicates the combustion of samples conforms to the rules of first order reaction. The experiments also shows that the activation energy is the lowest and the combustion blocking the weakest at 200℃ when the mix proportion is between 20% and 25%. Fitting straight line Key words: plastic waste, coal, blend-melt sample, kinetics 粉混合，在混熔温度 200 ℃下制成样品进行燃烧动 0 前言 力学试验。 现代社会, 由于塑料的优良特性,其制品获得了 1 燃烧动力学求解方法 日益广泛的应用。但是塑料制品使用后所产生的 “ 白色污染” 问题受到了广泛关注。如何实现废塑料 假设在无限短的时间间隔内，非等温过程可 的减量化、无害化、资源化利用处理,世界各国在 看着等温过程，样品的燃烧速率可表示为： 技术开发方面作了大量工作,并出现了多种废塑料 da/dt=KCn (1) 处理技术[1-4], 如再生利用、堆积后掩埋、焚烧、 引入 Arrhenius 公式 K=A*exp(-E/RT) 后得 燃料化，尤其是废塑料燃料化国内外进行了诸如 到： 煤与废塑料共焦化[5-8] 、高炉喷吹废旧塑料等研究。