DEFECTS SIMULATION OF ROLLING STRIP.docVIP

7 Materials Engineering, Vol. 16, 2009, No. 3 DEFECTS SIMULATION OF ROLLING STRIP 1 2 2 2 2 Rudolf Mi?i?ko , Tibor Kva?kaj , Martin Vlado , Lucia Gulová , Miloslav Lupták , Jana Bidulská2 Received 26 May 2009; accepted in revised form 8 June 2009 th th Abstract The defects in the continuous casting slabs can be developed or kept down in principle by rolling technology, especially depend to sort, size and distribution of primary defects, as well as used of rolling parameters. Scope of the article is on observation behavior artificial surface and undersurface defects (scores) without filler (surface defects) and filling by oxides and casting powder (subsurface defects). First phase of hot rolling process have been done by software simulation DEFORM 3D setting to the limited condition for samples with surface defects. Samples of material with low-carbon steel of sizes h x b x l have been chosen and the surface defects shape ?U” and ?V” of scores have been injected artificially by software. The process of rolling have been simulated on the deformation temperatures 1200°C and 900°C, whereas on the both of this deformation temperatures have been applied amount of deformation 10 and 50 %. With respect to the process of computer simulation, it is not possible to truthful real oxidation condition (physical – chemical process during heat of metal), in the second phase of our investigation have been observed influence of oxides and casting powders inside the scores for a defect behavior in plastic deformation process (hot and cold rolling process) in laboratory condition. The basic material was STN steel class 11 375, cladding material was steel on the bases C-Mn-Nb-V. Scores have been filled by scales to get from the heating temperatures (1100°C a 1250°C), varied types of casting