Precipitation hardening  Objective  The objective of this laboratory is for you to explore the kinetics and strengthening of Al by precipitation  hardening.  Preparation  Read sections 10.1‐10.5 of Meyers and Chawla.  Equipment and samples  • First week: Differential scanning calorimeters; ovens for heat treating Al alloys.  Second  week:  mechanical testing facilities in Talbot.    • Discs of Al 2024 alloy for DSC studies; bars of Al 2024 for tensile testing and hardness  testing.  • Computer, plotting software.  Introduction  Pure fcc metals such as Al have low yield strengths because the stress required to move a dislocation is  small.  One method of strengthening an alloy is through precipitation reactions.  Precipitation hardening  is the process of hardening or strengthening of an alloy by precipitating finely dispersed precipitates of  the solute in a supersaturated matrix.  This process involves the following three basic steps:  1.  The first step  is the solution  heat treatment or  homogenization.   Figure  1  illustrates this  phenomenon.  During this step, an alloy of composition X  is heated to a temperature T ,  1 1 between the solvus and solidus temperatures and soaked there until all of the solute dissolves  into the  α phase and a uniform solid‐solution structure is produced.  2.  The second step is quenching.  Quenching is simply cooling the sample rapidly to a lower  temperature, T3, usually room temperature, and the cooling medium is usually water at room  temperature.  During quenching, the solute is not immediately able to diffuse out of a phase and  the alloy is said to be supersaturated.  The rationale behind the quenching process is to preserve  the uniform soli