孙口黄河大桥技术总结.doc

孙口黄河大桥技术总结 篇一：孙口黄河大桥钢梁整体节点的焊接技术 孙口黄河大桥钢梁整体节点的焊接技术 孙昌茂 摘 要： 介绍了孙口黄河大桥整体节点的焊接特点。定位焊、不等厚对接焊、棱角焊、角接焊、平联节点板的焊接技术，消除了棱角焊等产生的咬边、沟槽、高温裂纹、烧穿和焊偏等问题，通过采用合理的焊接顺序，确保了整体节点的制造精度和焊接质量。 关键词： 黄河大桥；钢桥；节点板；整体节点；焊接工艺；定位焊；对接焊；角焊 中图分类号： U445.583 文献标识码： A文章编号： 1003-4722(1999)02-0044-02 The Welding Technique of Steel Beam Monolithic Gusset for Sunkou Yellow River Bridge SU N Chang-mao (Baoji Bridge Plant,Baoji 721006,China) Abstract: In this paper,the welding characteristics of monolithic gusset for Sunkou Yellow River Bridge were introduced.By use of welding technique,such as tack weld difference thick butt welding,angle welding fillet welding and the gusset plate welding of longitudinal level bracing,some problems,for example,undercut,flume and ditch,hot crack,burn through and lack of fusion,which was caused by angle welding were eliminated.By rational welding sequence,the manufacture precision and welding quality of the monolithic gusset were ensured. Key words: Yellow River Bridge；steel bridge；tack weld；butt welding；fillet welding；gusset plate；monolithic gusset;welding technology 1 前 言 孙口黄河大桥是京九线衡水-商丘的一座铁路双线下承式无竖杆三角桁式整体节点栓焊连续桁梁，跨度为4×180 m，共4联。整体节点为国内首次采用的新结构，具有节省钢材和高强度螺栓，有利于工地架设 等优点，是今后的发展方向。整体节点构造复杂，焊缝密集。既有对接焊缝，又有棱角焊缝和角焊缝，焊接质量要求高，屈服强度控制严，在焊接实验中还存在对接、棱角接熔深储备不够，棱角焊有沟槽、咬边、高温裂纹和烧穿等问题。在宝鸡桥梁厂和有关单位的共同努力下，使问题得到解决，确保了焊接质量，并提前一个多月完成。 2 孙口黄河大桥的焊接工艺研究 2.1 焊接接头的主要技术指标： 对接 σs(W)=σs(B)+100 (MPa);角接 σs(W)=σs(B)+120 (MPa); 各种焊接接头的三区 -25℃，AKV≥48J(35J)。 2.2 焊接工艺研究 对SM490C钢对接、棱角接、角接焊接工艺进行了研究。用优化的H08MnT或H10Mn2、H08MnA焊丝、SJ101焊剂和焊接工艺施焊各种焊接接头，按照修订后的技术指标衡量，得知H10Mn2焊丝能够满足对接、棱角接技术指标要求，H08MnA焊丝能够满足角接头技术指标的要求。 在焊接过程中，对熔深储备不够的焊缝，通过改变坡口尺寸、坡口角度和调整焊接参数，使之得到了改善；对棱角焊缝的沟槽和咬边问题，通过改变焊丝倾斜角度和焊丝对准位置，调整焊接顺序，使之得到了解决；对于棱角焊缝的第1道焊缝产生的高温裂纹，通过改变坡口尺寸，减小焊接电流，减慢车速，提高弧压或用CO2气体保护焊打底，使之得 到了解决。 3 孙口黄河大桥整体节点的焊接 3.1 整体节点的构造 孙口黄河大桥上下弦杆采用的整体节点，是由2块带节点的腹板、2块盖板、6块隔板和内撑板、接头板、平联节点板、各种连接板等部件组成。为了节省钢材，盖、腹板由不同尺寸和不同厚度的钢板拼接而成。 3.2 焊接 3.2.1 定位焊 为确保焊前部件的相互位置，防止部件倾倒进行了定位焊。因定位焊焊道短，冷却速度快，焊接热影响区易产生淬硬组织，从而形成冷裂纹。为此，用斜Y形坡口焊接