电池隔膜用HDPE微孔膜的制备和研究_耿忠民.pdf

研 究 与 设 计 电池隔膜用HDPE 微孔膜的制备和研究 耿忠民，张雪冰，叶 寅 （中国科学院上海应用物理研究所，上海201800） 摘要：以高密度聚乙烯（ HDPE ） 和邻苯二甲酸二丁酯（ DBP ） 作为膜材料和稀释剂，采用热致相分离法（ TIPS ） 制备 了用于电池隔膜材料的微孔膜。 通过对 HDPE /DBP 体系的相分离过程进行研究，绘制了 HDPE/DBP 体系的相图。 用 扫描电子显微镜（ SEM ） 研究了二元体系的相分离过程及聚合物浓度、冷却速率对膜断面微观结构的影响。 关键词：热致相分离；HDPE ；微孔膜 TM 912.9 A 1002- 087 X(2009)11- 0977- 03 中图分类号： 文献标识码： 文章编号： Preparation and research of HDPE microporous membrane for battery separators GENG Zhong-min, ZHANG Xue-bing, YE Yin (Shanghai Applied Physics Institute, Chinese Academy of Science, Shanghai 201800, China) Abstract: Microporous membrane for battery separators were prepared with HDPE and DBP by thermally induced phase separation (TIPS) method .The phase diagrams of HDPE with DBP were determined by researching the process of phase separation of HDPE with DBP. The effects of phase separation process, polymer concentration and cooling rate on membrane cross- section microstructures were characterized by SEM. Key words: TIPS; HDPE; microporous membrane 二次碱性电池是应用广泛的一种化学电源。隔膜是二次碱 聚乙烯微孔膜具有良好的抗酸碱能力，较好的抗撕裂强 性电池的心脏材料之一，其性能的优劣直接影响电池的使用性 度、且有较低的面电阻和良好的吸液保液能力，是电池隔膜的 [2] 能和循环寿命。隔膜的主要作用是: （1）隔离正负极并使电池 理想材料。Sun 等 采用高密度聚乙烯(HDPE)和液体石腊(LP) 内的电子不能自由穿过；（2）能够让离子（电解质液中）在正 为体系制备中空纤维微孔膜。实验结果表明随聚合物初始浓 负极间自由通过。电池隔膜的制备涉及高分子材料、精细化工 度增大，体系晶核数量增加，但在球晶内或球晶间的稀释剂液 等多个领域，难度较大。 目前国内常用的二次碱性电池隔膜主 滴数量和体积变小，萃取出稀释剂后孔径尺寸相应减小，同时 要依靠进口。